Kuraray Genestar™ GN2450 Nylon, 45% Glass Filled

Category Polymer , Thermoplastic , Nylon
Manufacturer Kuraray Company
Trade Name Genestar™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kuraray Genestar™ GN2450 Nylon, 45% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
High Strength V-0 Grade. Features a high strength and modulus. It is well suited for FPC sliders and IC sockets, as well as other components that require modulus and dimensional precision.
Physical Properties Metric English Comments
Specific Gravity 1.73 g/cc
1.73 g/cc
Water Absorption 0.70 %
0.70 %
Linear Mold Shrinkage, Flow 0.0010 cm/cm
0.0010 in/in
Linear Mold Shrinkage, Transverse 0.0050 cm/cm
0.0050 in/in
Melt Flow 15 g/10 min

@Load 2.16 kg,
Temperature 320 °C
15 g/10 min

@Load 4.76 lb,
Temperature 608 °F
ASTM D1238
Spiral Flow 3.70 cm

@Load 750 kg,
Temperature 320 °C
1.46 in

@Load 1650 lb,
Temperature 608 °F
0.5mm diameter
Mechanical Properties Metric English Comments
Tensile Strength 40.0 MPa
5800 psi
Weld; ASTM D638
200 MPa
29000 psi
ASTM D638
Elongation at Yield 0.40 %
0.40 %
Weld; ASTM D638
4.1 %
4.1 %
ASTM D638
Flexural Strength 270 MPa
39200 psi
ASTM D790
Flexural Modulus 14.0 GPa
2030 ksi
ASTM D790
Izod Impact, Notched 1.05 J/cm
1.97 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 306 °C
583 °F
Deflection Temperature at 1.8 MPa (264 psi) 285 °C
545 °F
ASTM D648
Glass Transition Temp, Tg 125 °C
257 °F
Flammability, UL94 V-0
V-0
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 3.8

@Frequency 1.00e+10 Hz
3.8

@Frequency 1.00e+10 Hz
ASTM D150
Dielectric Strength 30.0 kV/mm
762 kV/in
ASTM D149
Dielectric Loss Index 0.010

@Frequency 1.00e+10 Hz
0.010

@Frequency 1.00e+10 Hz
ASTM D150
Comparative Tracking Index >= 600 V
>= 600 V
ASTM UL746A