Polykemi AB SCANMID 6 B11^ F45 Nylon 6, Glass Fiber Reinforced

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Polykemi AB
Trade Name SCANMID 6
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polykemi AB SCANMID 6 B11^ F45 Nylon 6, Glass Fiber Reinforced.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polykemi AB
Physical Properties Metric English Comments
Density 1.51 g/cc
0.0546 lb/in³
ISO 1183
Filler Content 45 %
45 %
±2%; Polykemi
Linear Mold Shrinkage 0.0020 cm/cm
0.0020 in/in
With Flow; ISO 2577
0.0080 cm/cm
0.0080 in/in
Across Flow; ISO 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break <= 200 MPa
<= 29000 psi
ISO/R527
Flexural Strength <= 280 MPa
<= 40600 psi
ISO 178
Flexural Modulus 12.8 GPa

@Temperature 23.0 °C
 1860 ksi

@Temperature 73.4 °F
 ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
 NB

@Temperature 73.4 °F
 ISO 179
Charpy Impact, Notched 1.50 J/cm²

@Temperature 23.0 °C
 7.14 ft-lb/in²

@Temperature 73.4 °F
 ISO 179
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
120°C/h; ISO 75/1
Deflection Temperature at 1.8 MPa (264 psi) 210 °C
410 °F
120°C/h; ISO 75/1
Vicat Softening Point >= 200 °C

@Load 5.001 kg
 >= 392 °F

@Load 11.03 lb
 50°C/h; ISO 306
Flammability, UL94 HB

@Thickness 1.60 mm
 HB

@Thickness 0.0630 in
Glow Wire Test 650 °C

@Thickness 2.00 mm
 1200 °F

@Thickness 0.0787 in
 IEC 695-2-1