Kolon SPESIN® KP213G30 Flame Retardant PBT Resin
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), Flame Retardant |
| Manufacturer | Kolon |
| Trade Name | SPESIN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon SPESIN® KP213G30 Flame Retardant PBT Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SPESIN® is a thermoplastic PBT resin with excellent thermal, mechanical and electrical properties. SPESIN® is widely used in industrial parts and especially in electrical-electronic parts.High heat stability, outstanding abrasion resistance, excellent electrical properties, good surface gloss, low water absorption, excellent chemical resistance, good processabilityInformation provided by US distributor, API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | DIN 53479; ASTM D792 |
| Water Absorption | 0.050 % | 0.050 % | DIN 53475; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.010 cm/cm | 0.0050 - 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | DIN 53505; ASTM D785 |
| Tensile Strength, Ultimate | 137 MPa | 19900 psi | DIN 53455; ASTM D638 |
| Elongation at Break | 5.0 % | 5.0 % | DIN 53455; ASTM D638 |
| Flexural Yield Strength | 211 MPa | 30600 psi | DIN 53455; ASTM D790 |
| Flexural Modulus | 8.34 GPa | 1210 ksi | DIN 53452; ASTM D790 |
| Izod Impact, Notched | 0.883 J/cm | 1.65 ft-lb/in | DIN 53453; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
DIN 53752; ASTM D696 |
| Melting Point | 224 °C | 435 °F | DIN 53736; ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DIN 53461; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | DIN 53461; ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.2 @Frequency 1e+6 Hz |
3.2 @Frequency 1e+6 Hz |
ASTM D150/DIN 53483 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149/DIN 53481 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
Users viewing this material also viewed the following:
- NanoAmor 90%, OD: 1-2 nm OH Functionalized Single-Walled Carbon Nanotubes
- Kingfa JH960 HT10 Non-halogenated Flame Retardant PC/ABS Alloy
- Solvay TECHNYL® B 218L V20 Black 44 N PA66, 25% glass fiber, DRY
- Samsung Cheil Industries Starex® NT-7200 W ABS/PET, Unreinforced FR
- Tra-Con Tra-Bond 2114 Water White Transparent Epoxy Adhesive
- Dow Corning SILASTIC® 7-6840 BIOMEDICAL GRADE LSR, KIT
- Dow Corning SYL-OFF® 7041 RELEASE MODIFIER
- Chosun Refractories SCX-90IP Plastic Refractory
Copyright © lookpolymers.com All Rights Reserved