Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Film Grade
Manufacturer Braskem
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Braskem HF 0147 HDPE Blown Film Extrusion Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
38µm film gauge, obtained in 75mm extruder, die gap 1.0mm, output 1.75 kg/h-cm with 2:1 BUR. Applications: Grocery and T-shirt bags; merchandise bags; frozen-food bags. Information provided by Braskem
Physical Properties Metric English Comments
Density 0.947 g/cc
0.0342 lb/in³
ASTM D1505
Thickness 38.0 microns
1.50 mil
Melt Flow 0.30 g/10 min

@Load 5.00 kg,
Temperature 190 °C
0.30 g/10 min

@Load 11.0 lb,
Temperature 374 °F
ASTM D1238
High Load Melt Index 8.5 g/10 min

@Load 21.6 kg,
Temperature 190 °C
8.5 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 43.0 MPa
6240 psi
ASTM D882
Film Tensile Strength at Yield, TD 29.0 MPa
4210 psi
ASTM D882
Film Elongation at Break, MD 580 %
580 %
ASTM D882
Film Elongation at Break, TD 790 %
790 %
ASTM D882
Elmendorf Tear Strength, MD 0.500 g/micron
12.7 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 5.70 g/micron
145 g/mil
ASTM D1922
Dart Drop 4.34 g/micron
110 g/mil
ASTM D1709
Film Tensile Strength at Break, MD 84.0 MPa
12200 psi
ASTM D882
Film Tensile Strength at Break, TD 49.0 MPa
7110 psi
ASTM D882
Heat Seal Strength Initiation Temperature 125 °C
257 °F
Sealing Initial Temperature; Braskem® Method
Descriptive Properties Value Comments
Minimum Recommended Thickness 13 µm
Molecular Weight Distribution Bimodal
Puncture Strength 78 J/m
Braskem® Method