Sharadaa Ceramics VELECRETE RC 104 Rodding Castables
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Sharadaa Ceramics |
| Trade Name | VELECRETE |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sharadaa Ceramics VELECRETE RC 104 Rodding Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: The Rodding Castables offered by us are user friendly in nature and does not require high energy mixing machines and vibrators. Free flowing in nature, these castables are designed in compliance with international standards.Bond: UltrafineAggregate: Cal. BauxiteType of Setting: HydraulicInformation provided by Sharadaa Ceramics Pvt. Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.80 g/cc | 0.101 lb/in³ | After Drying at 110°C |
| Porosity | 16 - 18 % @Temperature 1300 °C |
16 - 18 % @Temperature 2370 °F |
|
| Grain Size | <= 10000 µm | <= 10000 µm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0180 GPa @Temperature 1000 °C |
2.61 ksi @Temperature 1830 °F |
Cold |
| 0.0200 GPa @Temperature 1100 °C |
2.90 ksi @Temperature 2010 °F |
Hot | |
| 0.0240 GPa @Temperature 1400 °C |
3.48 ksi @Temperature 2550 °F |
Cold | |
| 0.0240 GPa @Temperature 110 °C |
3.48 ksi @Temperature 230 °F |
Cold | |
| Compressive Strength | 90.0 MPa @Temperature 1000 °C |
13100 psi @Temperature 1830 °F |
Cold Crushing |
| 120 MPa @Temperature 110 °C |
17400 psi @Temperature 230 °F |
Cold Crushing | |
| 120 MPa @Temperature 1400 °C |
17400 psi @Temperature 2550 °F |
Cold Crushing |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 1.74 W/m-K @Temperature 600 °C |
12.1 BTU-in/hr-ft²-°F @Temperature 1110 °F |
Hot Face |
| Maximum Service Temperature, Air | 1600 °C | 2910 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 77 % | 77 % | |
| Fe2O3 | 1.5 % | 1.5 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Permanent Linear Change | <-0.5% | 1600°C |
| Thermal Expansion | 1.1 | at 1100°C |
| Thermal Shock Resistance | Excellent |
Users viewing this material also viewed the following:
- Polykemi AB SCANMID 6 B12^ F20 NH6 Nylon 6, Glass Fiber Reinforced, Halogen Free, Flame Retardant
- PSM Industries Ferro-TiC® CM High Chrome Tool Steel
- Iran Petrochemical (PCC) Bandar Imam Poliran LH0050 LDPE (discontinued **)
- Jackon JACKOCELL® S332 Expanded Polystyrene Packaging and Shape Molding
- Wellman Wellamid® XT1573-N Impact Modified Nylon 66
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 90 PHR Suprex Clay Filler
- EMS-Griltech Grilon® BM 20R Nylon 6 Monofilament (Medium-Set)
- 3M FP088 Clear Polypropylene Label Products
- ArcelorMittal 12 High formability steel for drawing, Hot rolled
- Resinlab® EP1026R Rubber Modified Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved