- Kolon KOPA® KN333NW High Impact Nylon 66
Kolon KOPA® KN333NW High Impact Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Impact Grade |
| Manufacturer | Kolon |
| Trade Name | Kopa® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kolon KOPA® KN333NW High Impact Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Impact -resistant, dimensional safetyApplications Wheel coversInformation provided by API-Kolon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.016 - 0.019 cm/cm | 0.016 - 0.019 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength | 59.0 MPa | 8560 psi | ASTM D638 |
| Elongation at Break | 50 % | 50 % | ASTM D638 |
| Flexural Strength | 98.0 MPa | 14200 psi | ASTM D790 |
| Flexural Modulus | 1.961 GPa | 284.4 ksi | ASTM D790 |
| Izod Impact, Notched | 5.88 J/cm | 11.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 60.0 µm/m-°C | 33.3 µin/in-°F | ASTM D696 |
| Melting Point | 255 °C | 491 °F | ASTM D1525 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ASTM D648 |
| Flammability, UL94 | HB | HB |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1 | 3.1 | ASTM D150 |
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | ASTM D149 |
| Arc Resistance | 125 sec | 125 sec | ASTM D495 |
Users viewing this material also viewed the following:
- Resin Technology Group UV-403 High Clarity, Structural Polycarbonate and PVC Bonder
- Karina E 800-10/1-A-ERYB-PO PVC Compound White Color
- Saint-Gobain CHR® 2255-3 High Modulus PTFE Film Backing Silicone Adhesive Pressure Sensitive Tape
- A. Schulman POLYBATCH™ White LL8970 TS Concentrate Based In LLDPE
- Total PPC 4660 Polypropylene, Heterophasic Copolymer
- ChevronTexaco Regal® 390
- Cadi 40 MOLD-MOR™
- 3M Novec™ 72DA Engineered Fluid
- BASF Sicopal® Blue K 6310 Color Additive
- Gwent Electronic Materials C2060602D1 Membrane Touch Switch Paste
Copyright © lookpolymers.com All Rights Reserved