SABIC Innovative Plastics LNP THERMOTUF VF004S PA 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP Thermotuf |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOTUF VF004S PA 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP THERMOTUF* VF004S is a compound based on Nylon resin containing Glass Fiber. Added features of this material include: Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.740 % | 0.740 % | 50% RH, 24 hrs; ASTM D570 |
| 1.10 % | 1.10 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0060 cm/cm @Time 86400 sec |
0.0040 - 0.0060 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0080 - 0.010 cm/cm @Time 86400 sec |
0.0080 - 0.010 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 97.0 MPa | 14100 psi | 5 mm/min; ISO 527 |
| 102 MPa | 14800 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 3.0 % | 3.0 % | Type I, 5 mm/min; ASTM D638 |
| 3.0 % | 3.0 % | 5 mm/min; ISO 527 | |
| Elongation at Yield | 2.6 % | 2.6 % | 5 mm/min; ISO 527 |
| 2.8 % | 2.8 % | Type I, 5 mm/min; ASTM D638 | |
| Tensile Modulus | 6.21 GPa | 901 ksi | 1 mm/min; ISO 527 |
| 6.47 GPa | 938 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 156 MPa | 22600 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 5.08 GPa | 737 ksi | 2 mm/min; ISO 178 |
| 5.62 GPa | 815 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 1.28 J/cm | 2.40 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 7.04 J/cm | 13.2 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 42.0 kJ/m² | 20.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 22.0 J @Temperature 23.0 °C |
16.2 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Impact Test | 6.00 J | 4.43 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 29.9 µm/m-°C @Temperature -30.0 - 30.0 °C |
16.6 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 81.2 µm/m-°C @Temperature -30.0 - 30.0 °C |
45.1 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 256 °C @Thickness 3.20 mm |
493 °F @Thickness 0.126 in |
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 235 °C | 455 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 240 °C @Thickness 3.20 mm |
464 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
Users viewing this material also viewed the following:
- Raschig Group 3535 Epoxy
- Guarniflon PTFE G415 Polytetrafluoroethylene 25% Soft Carbon
- Taiwan PU Corporation TPU-C75 General Grade, Calender Molding Polyester Base TPU
- SABIC Innovative Plastics Ultem AUT230M PEI (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL NH6010B PPE+HIPS (Europe-Africa-Middle East)
- SABIC Innovative Plastics NORYL ENV105 PPE+HIPS (Europe-Africa-Middle East)
- A. Schulman POLYFLAM™ E-17338 22% CACO3 Filled Copolymer Polypropylene
- Covestro Desmopan® 460 Thermoplastic Polyurethane
- Ascend Performance Materials Vydyne® 50BW Nylon 66, Dry as Molded
- Overview of materials for Polyether Ester Elastomer
Copyright © lookpolymers.com All Rights Reserved