Kingfa PA66-G15 15% Glass Fiber Reinforced PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 20% Glass Fiber Filled |
| Manufacturer | Kingfa Sci. & Tech. Co. |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Kingfa PA66-G15 15% Glass Fiber Reinforced PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Features:Good size stabilityLow tendency to wrapHigh mechanical propertiesGood low temperature resistanceGood surfaceExcellent balance propertiesApplications:Injection moldingAutomobile partsPower toolsMachinery partsSport applianceInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.24 g/cc @Temperature 23.0 °C |
1.24 g/cc @Temperature 73.4 °F |
ASTM D792 |
| Water Absorption | 0.60 % @Temperature 23.0 °C, Time 86400 sec |
0.60 % @Temperature 73.4 °F, Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.012 cm/cm @Temperature 23.0 °C |
0.0050 - 0.012 in/in @Temperature 73.4 °F |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 119 | 119 | ASTM D785 |
| Tensile Strength at Break | 130 MPa | 18900 psi | 10mm/min; ASTM D638 |
| Flexural Strength | 180 MPa | 26100 psi | 2mm/min; ASTM D790 |
| Flexural Modulus | 6.10 GPa | 885 ksi | 2mm/min; ASTM D790 |
| Izod Impact, Notched | 0.850 J/cm @Thickness 3.20 mm, Temperature 23.0 °C |
1.59 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 253 °C @Thickness 6.40 mm |
487 °F @Thickness 0.252 in |
ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C @Thickness 6.40 mm |
469 °F @Thickness 0.252 in |
ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+16 ohm-cm | 1.00e+16 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | <= 310 °C | <= 590 °F | |
| Rear Barrel Temperature | 260 - 280 °C | 500 - 536 °F | Start Point: 265°C |
| Middle Barrel Temperature | 265 - 300 °C | 509 - 572 °F | Start Point: 285°C |
| Front Barrel Temperature | 275 - 305 °C | 527 - 581 °F | Start Point: 285°C |
| Melt Temperature | 275 - 310 °C | 527 - 590 °F | Start Point: 285°C |
| Mold Temperature | 50.0 - 80.0 °C | 122 - 176 °F | Start Point: 60°C |
| Drying Temperature | 90.0 - 110 °C @Time 14400 - 21600 sec |
194 - 230 °F @Time 4.00 - 6.00 hour |
Pre-dry |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Glass Fiber Content (%) | 15 | |
| Injection Speed | Moderate to High |
Users viewing this material also viewed the following:
- NOVA Chemicals EPS 34RA Regular Expandable Polystyrene
- Hexion Bakelite™ PF 51 Phenolic Formaldehyde Resin, Special Preparation Cylindrical Pellets (discontinued **)
- JPJ Technologies 2100J HDPE Extrusion
- Karina 828-08/20-AY-ERYB-PO Beige PVC Compound
- Techmer ES Luriblend® PA6/6 GF10 M/TL10 10% Glass Filled
- SABIC Innovative Plastics LNP Thermocomp PF0069 PA 6 (Europe-Africa-Middle East)
- Borealis Borstar® HE3496-LS Yellow Polyethylene Compound for The Coextrusion of Identifying Stripes On Black HD Pipe for Natural Gas
- Hexcel® HexForce™ 7628 Fiber Glass Fabric
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer, Hardness 83A
Copyright © lookpolymers.com All Rights Reserved