North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade

Category Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Wood Filled
Manufacturer North Wood Plastics
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF North Wood Plastics Polypropylene with 60% Wood Fiber, Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by North Wood Plastics, Inc.
Physical Properties Metric English Comments
Density 1.145 g/cc
0.04137 lb/in³
ASTM D792
Linear Mold Shrinkage 0.0018 cm/cm
0.0018 in/in
ASTM D955
Melt Flow <= 0.50 g/10 min

@Temperature 190 °C
 <= 0.50 g/10 min

@Temperature 374 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 20.0 MPa
2900 psi
ASTM D638
Elongation at Break 1.2 %
1.2 %
ASTM D638
Tensile Modulus 6.20 GPa
899 ksi
ASTM D638
Flexural Yield Strength 39.0 MPa
5660 psi
ASTM D790
Flexural Modulus 4.90 GPa
711 ksi
1% Secant at 0.05 in/min; ASTM D790
Izod Impact, Notched 0.230 J/cm
0.431 ft-lb/in
ASTM D256
Izod Impact, Unnotched 0.400 J/cm
0.749 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 36.0 µm/m-°C

@Temperature 20.0 °C
 20.0 µin/in-°F

@Temperature 68.0 °F
Deflection Temperature at 1.8 MPa (264 psi) 98.0 °C
208 °F
ASTM D648
Processing Properties Metric English Comments
Processing Temperature <= 200 °C
<= 392 °F
To prevent fiber degradation.