Kingfa PA6-MG45 45% Glass & Mineral Filled PA6

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 50% Glass Fiber Filled
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa PA6-MG45 45% Glass & Mineral Filled PA6.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Low tendency to wrapExcellent size stabilityLow abrasionOutstanding surfaceApplications:Injection moldingAutomobile partsInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.48 g/cc

@Temperature 23.0 °C
1.48 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.60 %

@Temperature 23.0 °C,
Time 86400 sec
0.60 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0030 cm/cm

@Temperature 23.0 °C
0.0020 - 0.0030 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 121
121
ASTM D785
Tensile Strength at Break 130 MPa
18900 psi
10mm/min; ASTM D638
Elongation at Break 2.0 %
2.0 %
10mm/min; ASTM D638
Flexural Strength 207 MPa
30000 psi
2mm/min; ASTM D790
Flexural Modulus 0.910 GPa
132 ksi
2mm/min; ASTM D790
Izod Impact, Notched 1.85 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
3.47 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 219 °C

@Thickness 6.40 mm
426 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 212 °C

@Thickness 6.40 mm
414 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Processing Properties Metric English Comments
Processing Temperature <= 300 °C
<= 572 °F
Rear Barrel Temperature 225 - 245 °C
437 - 473 °F
Start Point: 230°C
Middle Barrel Temperature 250 - 270 °C
482 - 518 °F
Start Point: 255°C
Front Barrel Temperature 260 - 280 °C
500 - 536 °F
Start Point: 265°C
Melt Temperature 255 - 285 °C
491 - 545 °F
Start Point: 265°C
Mold Temperature 50.0 - 70.0 °C
122 - 158 °F
Start Point: 60°C
Drying Temperature 90.0 - 110 °C

@Time 14400 - 21600 sec
194 - 230 °F

@Time 4.00 - 6.00 hour
Pre-dry
Descriptive Properties Value Comments
Glass Fiber Content (%) 45
Injection Speed Moderate to High