Kingfa MAC-501DY Modified PC/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Kingfa Sci. & Tech. Co.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Kingfa MAC-501DY Modified PC/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Features:Excellent balance propertiesGood low temperature impact strengthGood electro-plating propertiesGood processing propertiesApplications:Injection moldingAutomobile license platePower toolComputer and accessoriesMobile CD, DVDInformation Provided by Kingfa Sci. & Tech. Co., Ltd.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc

@Temperature 23.0 °C
1.13 g/cc

@Temperature 73.4 °F
ASTM D792
Water Absorption 0.10 %

@Temperature 23.0 °C,
Time 86400 sec
0.10 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm

@Temperature 23.0 °C
0.0040 - 0.0060 in/in

@Temperature 73.4 °F
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength at Break 55.0 MPa
7980 psi
50mm/min; ASTM D638
Elongation at Break >= 50 %
>= 50 %
50mm/min; ASTM D638
Flexural Strength 81.0 MPa
11700 psi
2mm/min; ASTM D790
Flexural Modulus 2.24 GPa
325 ksi
2mm/min; ASTM D790
Izod Impact, Notched 4.55 J/cm

@Thickness 3.20 mm,
Temperature 23.0 °C
8.52 ft-lb/in

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Izod Impact, Unnotched NB

@Thickness 3.20 mm,
Temperature 23.0 °C
NB

@Thickness 0.126 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 0.46 MPa (66 psi) 124 °C

@Thickness 6.40 mm
255 °F

@Thickness 0.252 in
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 108 °C

@Thickness 6.40 mm
226 °F

@Thickness 0.252 in
ASTM D648
Flammability, UL94 HB

@Thickness 1.60 mm
HB

@Thickness 0.0630 in
HB

@Thickness 3.20 mm
HB

@Thickness 0.126 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+16 ohm-cm
1.00e+16 ohm-cm
ASTM D257
Surface Resistance 1.00e+15 ohm
1.00e+15 ohm
ASTM D257
Dielectric Strength 28.0 kV/mm
711 kV/in
1.6mm; ASTM D149
Processing Properties Metric English Comments
Processing Temperature <= 260 °C
<= 500 °F
Rear Barrel Temperature 220 - 235 °C
428 - 455 °F
Start Point: 230°C
Middle Barrel Temperature 220 - 240 °C
428 - 464 °F
Start Point: 235°C
Front Barrel Temperature 230 - 250 °C
446 - 482 °F
Start Point: 240°C
Melt Temperature 220 - 240 °C
428 - 464 °F
Start Point: 235°C
Mold Temperature 40.0 - 80.0 °C
104 - 176 °F
Start Point: 60°C
Drying Temperature 90.0 - 105 °C

@Time 14400 - 21600 sec
194 - 221 °F

@Time 4.00 - 6.00 hour
Pre-dry
Back Pressure 0.300 - 1.00 MPa
43.5 - 145 psi
Descriptive Properties Value Comments
Injection Speed 60-90%