DuPont Performance Polymers Hytrel® 6356 Polyester Elastomer TPC-ET  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polyester Thermoplastic Elastomer
Manufacturer DuPont Performance Polymers
Trade Name Hytrel®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Hytrel® 6356 Polyester Elastomer TPC-ET  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
63 Shore D High Performance Polyester ElastomerInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
1.22 g/cc
0.0441 lb/in³
ISO 1183
Water Absorption 0.60 %

@Thickness 2.00 mm
 0.60 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Water Absorption at Saturation 0.50 %
0.50 %
Immersion 24h; ASTM D570
Viscosity 79580 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 79580 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
87700 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 87700 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
97070 cP

@Shear Rate 5000 1/s,
Temperature 230 °C
 97070 cP

@Shear Rate 5000 1/s,
Temperature 446 °F
 ISO 11403-1 -2
282300 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 282300 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
333010 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 333010 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
392200 cP

@Shear Rate 500 1/s,
Temperature 230 °C
 392200 cP

@Shear Rate 500 1/s,
Temperature 446 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 8.5 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 8.5 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 cm³/10min; ISO 1133
9.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
 9.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
 ISO 1133
Mechanical Properties Metric English Comments
Hardness, Shore D 57
57
15s; ISO 868
<= 63
<= 63
ISO 868
Tensile Strength at Break 43.0 MPa
6240 psi
ISO 527-1/-2
Tensile Stress 12.0 MPa

@Strain 5.00 %
 1740 psi

@Strain 5.00 %
 ISO 527-1/-2
15.0 MPa

@Strain 10.0 %
 2180 psi

@Strain 10.0 %
 ISO 527-1/-2
18.8 MPa

@Strain 50.0 %
 2730 psi

@Strain 50.0 %
 ISO 527-1/-2
19.0 MPa

@Strain 100 %
 2760 psi

@Strain 100 %
 ISO 527-1/-2
2.93 MPa

@Strain 5.00 %,
Temperature 150 °C
 425 psi

@Strain 5.00 %,
Temperature 302 °F
 ISO 11403-1 -2
4.62 MPa

@Strain 7.11 %,
Temperature 150 °C
 670 psi

@Strain 7.11 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
5.47 MPa

@Strain 20.0 %,
Temperature 150 °C
 793 psi

@Strain 20.0 %,
Temperature 302 °F
 ISO 11403-1 -2
5.51 MPa

@Strain 7.29 %,
Temperature 120 °C
 799 psi

@Strain 7.29 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
6.18 MPa

@Strain 17.14 %,
Temperature 150 °C
 896 psi

@Strain 17.14 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.38 MPa

@Strain 6.97 %,
Temperature 100 °C
 925 psi

@Strain 6.97 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
6.50 MPa

@Strain 26.33 %,
Temperature 150 °C
 943 psi

@Strain 26.33 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.53 MPa

@Strain 36.36 %,
Temperature 150 °C
 947 psi

@Strain 36.36 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.53 MPa

@Strain 46.39 %,
Temperature 150 °C
 947 psi

@Strain 46.39 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.57 MPa

@Strain 58.93 %,
Temperature 150 °C
 953 psi

@Strain 58.93 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.62 MPa

@Strain 72.3 %,
Temperature 150 °C
 960 psi

@Strain 72.3 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.68 MPa

@Strain 85.68 %,
Temperature 150 °C
 969 psi

@Strain 85.68 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.75 MPa

@Strain 98.22 %,
Temperature 150 °C
 979 psi

@Strain 98.22 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
6.98 MPa

@Strain 118.28 %,
Temperature 150 °C
 1010 psi

@Strain 118.28 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
7.12 MPa

@Strain 130.82 %,
Temperature 150 °C
 1030 psi

@Strain 130.82 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
7.17 MPa

@Strain 7.11 %,
Temperature 90.0 °C
 1040 psi

@Strain 7.11 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
7.51 MPa

@Strain 147.53 %,
Temperature 150 °C
 1090 psi

@Strain 147.53 %,
Temperature 302 °F
 TPE; ISO 11403-1 -2
7.65 MPa

@Strain 17.27 %,
Temperature 120 °C
 1110 psi

@Strain 17.27 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.26 MPa

@Strain 27.24 %,
Temperature 120 °C
 1200 psi

@Strain 27.24 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.38 MPa

@Strain 37.22 %,
Temperature 120 °C
 1220 psi

@Strain 37.22 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.40 MPa

@Strain 47.19 %,
Temperature 120 °C
 1220 psi

@Strain 47.19 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.47 MPa

@Strain 60.24 %,
Temperature 120 °C
 1230 psi

@Strain 60.24 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.61 MPa

@Strain 74.05 %,
Temperature 120 °C
 1250 psi

@Strain 74.05 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.74 MPa

@Strain 87.1 %,
Temperature 120 °C
 1270 psi

@Strain 87.1 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.89 MPa

@Strain 100.14 %,
Temperature 120 °C
 1290 psi

@Strain 100.14 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
8.92 MPa

@Strain 6.99 %,
Temperature 60.0 °C
 1290 psi

@Strain 6.99 %,
Temperature 140 °F
 TPE; ISO 11403-1 -2
9.08 MPa

@Strain 5.00 %,
Temperature 23.0 °C
 1320 psi

@Strain 5.00 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.15 MPa

@Strain 120.1 %,
Temperature 120 °C
 1330 psi

@Strain 120.1 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.16 MPa

@Strain 17.23 %,
Temperature 100 °C
 1330 psi

@Strain 17.23 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.42 MPa

@Strain 133.91 %,
Temperature 120 °C
 1370 psi

@Strain 133.91 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.84 MPa

@Strain 26.77 %,
Temperature 100 °C
 1430 psi

@Strain 26.77 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
9.94 MPa

@Strain 150.02 %,
Temperature 120 °C
 1440 psi

@Strain 150.02 %,
Temperature 248 °F
 TPE; ISO 11403-1 -2
9.98 MPa

@Strain 47.3 %,
Temperature 100 °C
 1450 psi

@Strain 47.3 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.0 MPa

@Strain 37.03 %,
Temperature 100 °C
 1450 psi

@Strain 37.03 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.04 MPa

@Strain 60.5 %,
Temperature 100 °C
 1456 psi

@Strain 60.5 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.05 MPa

@Strain 16.83 %,
Temperature 90.0 °C
 1458 psi

@Strain 16.83 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.2 MPa

@Strain 73.7 %,
Temperature 100 °C
 1480 psi

@Strain 73.7 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.35 MPa

@Strain 86.9 %,
Temperature 100 °C
 1501 psi

@Strain 86.9 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.51 MPa

@Strain 100.1 %,
Temperature 100 °C
 1524 psi

@Strain 100.1 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.79 MPa

@Strain 27.31 %,
Temperature 90.0 °C
 1565 psi

@Strain 27.31 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.81 MPa

@Strain 120.63 %,
Temperature 100 °C
 1568 psi

@Strain 120.63 %,
Temperature 212 °F
 TPE; ISO 11403-1 -2
10.82 MPa

@Strain 46.76 %,
Temperature 90.0 °C
 1569 psi

@Strain 46.76 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.88 MPa

@Strain 37.04 %,
Temperature 90.0 °C
 1578 psi

@Strain 37.04 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2
10.9 MPa

@Strain 60.23 %,
Temperature 90.0 °C
 1580 psi

@Strain 60.23 %,
Temperature 194 °F
 TPE; ISO 11403-1 -2