KEP Kepital® FG2025 25% Glass Fiber Reinforced Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, 30% Glass Fiber Reinforced |
| Manufacturer | Korea Engineering Plastics Co., Ltd. |
| Trade Name | Kepital® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | KEP Kepital® FG2025 25% Glass Fiber Reinforced Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by US distributor Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.59 g/cc | 0.0574 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | 24 hours at 73°F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 136.8 MPa @Thickness 3.17 mm |
19840 psi @Thickness 0.125 in |
|
| Elongation at Break | 3.0 % @Thickness 3.17 mm |
3.0 % @Thickness 0.125 in |
|
| Flexural Yield Strength | 205.2 MPa @Thickness 3.17 mm |
29760 psi @Thickness 0.125 in |
|
| Flexural Modulus | 9.03 GPa @Thickness 3.17 mm |
1310 ksi @Thickness 0.125 in |
|
| Izod Impact, Notched | 0.960 J/cm @Thickness 3.17 mm |
1.80 ft-lb/in @Thickness 0.125 in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 203 °C | 397 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 164 °C | 327 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 163 °C | 325 °F | ASTM D648 |
| Flammability, UL94 | HB @Thickness 1.59 mm |
HB @Thickness 0.0625 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 165 - 180 °C | 329 - 356 °F | |
| Middle Barrel Temperature | 175 - 195 °C | 347 - 383 °F | |
| Front Barrel Temperature | 180 - 195 °C | 356 - 383 °F | |
| Nozzle Temperature | 180 - 195 °C | 356 - 383 °F | |
| Melt Temperature | 185 - 220 °C | 365 - 428 °F | |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 80.0 - 90.0 °C | 176 - 194 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 48.3 - 117 MPa | 7000 - 17000 psi |
Users viewing this material also viewed the following:
- Abatron AboWeld 8101-7/AboCure 8101-7 Epoxy (discontinued **)
- Sax Polymers SAXAMID 126F9 Nylon 6, 45% Glass Fiber
- Wellman Wellamid® 22LH-N Unfilled Nylon 66, Lubricated & Heat Stabilized
- A. Schulman SCHULADUR® A GF30 30% Glass Fiber Reinforced PBT
- CoorsTek PolyGlyde™ 3000 Self-Lubricating Seal
- DuPont™ Tedlar® TWH20BS3 Satin White Polyvinyl Fluoride Film
- Hippe SI GC 201 Woven Glass Cloth Reinforced Silicone Resin - Sheet
- ChevronTexaco Delo® 3000 Marine Engine Oil, SAE 40
- Barlog Plastics KEBAFLEX U A 85 HT B01 natural TPU, Shore A85, natural, high temperature resistance
- 3M Dyneon™ TF 1750 PTFE
Copyright © lookpolymers.com All Rights Reserved