Inno-Comp INNOPOL® CS 3-8000 FR Flame Retardant Polypropylene Blend
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Flame Retardant |
| Manufacturer | Inno-Comp Ltd |
| Trade Name | INNOPOL® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Inno-Comp INNOPOL® CS 3-8000 FR Flame Retardant Polypropylene Blend.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
INNOPOL® CS 3-8000 FR is a flame retarded polypropylene compound based on a specific blend of polypropylene homo polymer and copolymer. This grade is available in natural and custom colored form.INNOPOL® CS 3-8000 FR is highly suitable for manufacturing indoor waste water discharge system parts. This grade is a flame-retarded material, where the classification of flame retardancy is B2 according to DIN 4102.Information provided by INNO-COMP
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.930 g/cc | 0.0336 lb/in³ | ISO 1183 |
| Melt Flow | 0.60 g/10 min @Load 2.16 kg, Temperature 230 °C |
0.60 g/10 min @Load 4.76 lb, Temperature 446 °F |
nozzle diam 2.095 mm; ISO 1133 |
| Storage Temperature | <= 60.0 °C | <= 140 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 28.0 MPa | 4060 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Yield | 11 % | 11 % | 50 mm/min; ISO 527-1,-2 |
| Tensile Modulus | 1.10 GPa | 160 ksi | 1 mm/min; ISO 527-1,-2 |
| Charpy Impact, Notched | 0.250 J/cm² @Temperature -20.0 °C |
1.19 ft-lb/in² @Temperature -4.00 °F |
ISO 179/1eA |
| 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 °C | 194 °F | ISO 75-1,-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Middle Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Front Barrel Temperature | 180 - 220 °C | 356 - 428 °F | Extrusion |
| 190 - 260 °C | 374 - 500 °F | Injection | |
| Die Temperature | 190 - 220 °C | 374 - 428 °F | Extrusion |
| Melt Temperature | 200 - 230 °C | 392 - 446 °F | Extrusion |
| 240 - 260 °C | 464 - 500 °F | Injection | |
| Mold Temperature | 15.0 - 50.0 °C | 59.0 - 122 °F | |
| Moisture Content | <= 0.050 % | <= 0.050 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Designation | PP-H/PP-B | ISO 1043 |
Users viewing this material also viewed the following:
- Quadrant EPP Semitron® ESd 520HR (ASTM Product Data Sheet)
- Cookson Group Plaskon® 435 Mineral Filled Epoxy Molding Compound (discontinued **)
- Huntsman DY 9577 Epoxy Accelerator
- Lehmann & Voss LUVOCOM® 1105-0918/EM/BL PEEK, with glass fiber
- SABIC Innovative Plastics XYLEX X7300CL PC+POLYESTER
- Master Bond EP36CLV One Component Heat Resistant Liquid Flexible Epoxy
- A. Schulman PP 984 Polypropylene Medium Impact Polypropylene
- ExxonMobil Mobil ATF D/M
- Alliance C-5 Strontium Ferrite Ceramic Magnetic Material
- Overview of materials for Linear Medium Density Polyethylene (LMDPE), Rotational Molded
Copyright © lookpolymers.com All Rights Reserved