Albis Plastics Cellulose Acetate CA700 , Unreinforced, 25% Plasticizer (discontinued **)

Category	Polymer , Renewable/Recycled Polymer , Thermoplastic , Cellulosic , Cellulose Acetate, Molded
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Albis Plastics Cellulose Acetate CA700 , Unreinforced, 25% Plasticizer (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Amorphous Cellulose Acetate (CA)Characteristics: Chemical Resistance, Toughness, Strength, Hardness, Gloss, Clarity and "Feel"Applications: Tool Handles, Optical Products, Toys and Sheet ProductsProcessing: Injection Molding (Melt Temperature: 470°F, Mold Temperature: 160°F)Data supplied by ALBIS Plastics Corporation.

Physical Properties	Metric	English	Comments
Density	1.28 g/cc	0.0462 lb/in³	ASTM D792
Water Absorption	2.3 %	2.3 %	(24 hr); ASTM D570
Linear Mold Shrinkage	0.0020 - 0.0060 cm/cm	0.0020 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	40.7 MPa	5900 psi	ASTM D638
Tensile Strength, Yield	37.2 MPa	5400 psi	ASTM D638
Elongation at Break	25 %	25 %	ASTM D638
Flexural Yield Strength	62.7 MPa	9090 psi	ASTM D790
Flexural Modulus	2.34 GPa	339 ksi	ASTM D790
Izod Impact, Notched	1.60 J/cm	3.00 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	77.0 °C	171 °F	ASTM D648
Vicat Softening Point	113 °C	235 °F	ASTM D1525

Processing Properties	Metric	English	Comments
Melt Temperature	243 °C	469 °F	Injection Molding
Mold Temperature	71.0 °C	160 °F