Ineos Barex® 210 E Acrylonitrile-Methyl Acrylate Copolymer
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylic (PMMA) , Acrylonitrile-Methyl Acrylate Copolymer |
| Manufacturer | Ineos Olefins & Polymers USA |
| Trade Name | Barex® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos Barex® 210 E Acrylonitrile-Methyl Acrylate Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Extrusion Grade. Barex® Resins are available in either natural or blue tint. Barex® 210E is most commonly used for thermoformed sheet applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | |
| Apparent Bulk Density | 0.670 g/cc | 0.0242 lb/in³ | |
| Moisture Vapor Transmission | 3.00 cc-mm/m²-24hr-atm | 7.62 cc-mil/100 in²-24hr-atm | |
| Oxygen Transmission | 0.600 cc-mm/m²-24hr-atm | 1.52 cc-mil/100 in²-24hr-atm | |
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | ASTM D955 |
| Melt Flow | 3.0 g/10 min @Load 12.5 kg, Temperature 200 °C |
3.0 g/10 min @Load 27.6 lb, Temperature 392 °F |
2 mm x 8 mm |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 60 | 60 | |
| Hardness, Rockwell R | 115 | 115 | |
| Hardness, Shore D | 86 | 86 | |
| Tensile Strength, Yield | 65.0 MPa | 9430 psi | |
| Elongation at Break | 3.0 % | 3.0 % | |
| Flexural Yield Strength | 95.0 MPa | 13800 psi | |
| Flexural Modulus | 3.40 GPa | 493 ksi | |
| Compressive Yield Strength | 83.0 MPa | 12000 psi | |
| Izod Impact, Notched | 5.00 J/cm | 9.37 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.80 J/g-°C | 0.430 BTU/lb-°F | |
| Thermal Conductivity | 0.690 W/m-K | 4.79 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.0 °C | 171 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 69.0 °C | 156 °F | ASTM D648 |
| Vicat Softening Point | 83.0 °C | 181 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.511 | 1.511 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.90e+15 ohm-cm | 1.90e+15 ohm-cm | |
| Surface Resistance | >= 2.00e+17 ohm | >= 2.00e+17 ohm | |
| Dielectric Constant | 5.2 @Frequency 100 Hz |
5.2 @Frequency 100 Hz |
|
| Dissipation Factor | 0.070 @Frequency 100 Hz |
0.070 @Frequency 100 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 200 °C | 392 °F |
Users viewing this material also viewed the following:
- MV Labs PT167 Li2Pt(CN)4·xH2O Lithium tetracyanoplatinate(II) hydrate
- Polimeros Mexicanos Rotolene® Industrial Black Linear Medium Density Polyethylene
- Minelco MagniF Magnetite
- Solvay GEROPON® TK 32 Surfactant
- Elmer's Products Aron Alpha® 212E Cyanoacrylate Adhesive (Industrial Krazy Glue™)
- DuPont Performance Polymers Kalrez® Spectrum™ 7090 Fluoroelastomer
- Axiall 3014 Rigid PVC, Extrusion
- AK Steel Aluminized Carbon Steel, Extra Deep Drawing Steel (EDDS), Standard Grade
- A. Schulman ComAlloy Comtuf® 413 Glass Reinforced, Polycarbonate/Polyester Alloy, UL
- Albis Plastics Cellulose Acetate Butyrate B9024 (UVI, Odor Mask Added), 16% Plasticizer (discontinued **)
Copyright © lookpolymers.com All Rights Reserved