Polymer Resources PPX-FR2-[color]-EN Modified-PPO, V-1 Flame Retardant, Extrusion Grade

Category	Polymer , Thermoplastic , Polyphenylene Ether/PPO , Polyphenylene Ether, Heat Resistant
Manufacturer	Polymer Resources, LTD
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polymer Resources PPX-FR2-[color]-EN Modified-PPO, V-1 Flame Retardant, Extrusion Grade.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Modified-Polyphenylene Oxide, V-1 Flame Retardant, 210F HDT, Extrusion GradeFeatures: • Bromine Free • Chlorine FreeProcess: ExtrusionNotes: All physical, mechanical and thermal testing conducted on 1/8-inch thick, un-pigmented, test samples.Information provided by Polymer Resources Corporation.

Physical Properties	Metric	English	Comments
Specific Gravity	1.09 g/cc	1.09 g/cc	ASTM D792
Linear Mold Shrinkage	0.0050 - 0.0070 cm/cm	0.0050 - 0.0070 in/in	ASTM D955
Melt Flow	20 - 40 g/10 min @Load 11.6 kg, Temperature 250 °C	20 - 40 g/10 min @Load 25.6 lb, Temperature 482 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell R	115	115	ASTM D785
Tensile Strength at Break	49.0 MPa	7100 psi	ASTM D638
Tensile Strength, Yield	50.3 MPa	7300 psi	ASTM D638
Elongation at Break	35 %	35 %	ASTM D638
Flexural Strength	82.7 MPa	12000 psi	ASTM D790
Flexural Modulus	2.41 GPa	350 ksi	ASTM D790
Izod Impact, Notched	1.33 J/cm @Temperature -40.0 °C	2.50 ft-lb/in @Temperature -40.0 °F	ASTM D256
	2.67 J/cm @Temperature 22.8 °C	5.00 ft-lb/in @Temperature 73.0 °F	ASTM D256
Gardner Impact	16.9 J	12.5 ft-lb	ASTM D3029

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	98.9 °C	210 °F	ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	93.3 °C	200 °F	ASTM D648
UL RTI, Electrical	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 5.99 mm	149 °F @Thickness 0.236 in	UL 746
UL RTI, Mechanical with Impact	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 5.99 mm	149 °F @Thickness 0.236 in	UL 746
UL RTI, Mechanical without Impact	65.0 °C @Thickness 3.00 mm	149 °F @Thickness 0.118 in	UL 746
	65.0 °C @Thickness 5.99 mm	149 °F @Thickness 0.236 in	UL 746
Flammability, UL94	V-1 @Thickness 1.70 mm	V-1 @Thickness 0.0669 in
	V-1 @Thickness 3.00 mm	V-1 @Thickness 0.118 in

Processing Properties	Metric	English
Rear Barrel Temperature	>= 177 °C	>= 350 °F
Middle Barrel Temperature	>= 193 °C	>= 380 °F
Front Barrel Temperature	>= 193 °C	>= 380 °F
Melt Temperature	199 - 227 °C	390 - 440 °F
Drying Temperature	98.9 - 104 °C	210 - 220 °F
Dry Time	3.00 - 4.00 hour	3.00 - 4.00 hour

Descriptive Properties	Value	Comments
Vent	0.001