Ineos ABS Triax® 3050 ABS/Nylon Alloy, Injection Molding Grade (Conditioned)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS)/Nylon Blend , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 3050 ABS/Nylon Alloy, Injection Molding Grade (Conditioned).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Triax® 3050 resin is an ABS (Acrylonitrile Butadiene Styrene)/Nylon 6 alloy for injection molding. It is a semicrystalline thermoplastic with improved stability to light exposure, excellent processability, good chemical resistance, good fatigue performance, and excellent abrasion characteristics. Triax® 3050 resin exhibits a good balance of impact strength and flow properties. Typical applications include interior automotive applications.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ASTM-D792 |
| Density | 1.05 g/cc | 0.0380 lb/in³ | ASTM-D792 |
| Water Absorption | 1.1 % @Time 86400 sec |
1.1 % @Time 24.0 hour |
ASTM-D570 |
| Water Absorption at Saturation | 4.3 % | 4.3 % | ASTM-D570 |
| Linear Mold Shrinkage | 0.0090 cm/cm | 0.0090 in/in | ASTM-D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM-D955 |
| Melt Flow | 6.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
6.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
ASTM-D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 | 90 | ASTM-D785 |
| Tensile Strength, Yield | 40.0 MPa | 5800 psi | ASTM-D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM-D638 |
| Tensile Modulus | 2.03 GPa | 295 ksi | ASTM-D638 |
| Flexural Yield Strength | 56.9 MPa | 8250 psi | ASTM-D790 |
| Flexural Modulus | 1.17 GPa | 170 ksi | ASTM-D790 |
| Izod Impact, Notched | 0.747 J/cm @Thickness 6.35 mm, Temperature -40.0 °C |
1.40 ft-lb/in @Thickness 0.250 in, Temperature -40.0 °F |
ASTM-D256 |
| 0.801 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.50 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM-D256 | |
| 7.47 J/cm @Thickness 6.35 mm, Temperature 22.8 °C |
14.0 ft-lb/in @Thickness 0.250 in, Temperature 73.0 °F |
ASTM-D256 | |
| 8.01 J/cm @Thickness 3.17 mm, Temperature 22.8 °C |
15.0 ft-lb/in @Thickness 0.125 in, Temperature 73.0 °F |
ASTM-D256 | |
| Impact Test | 59.7 J @Temperature -40.0 °C |
44.0 ft-lb @Temperature -40.0 °F |
Instrumented Impact, Total Energy: 0.100-in.; 0.5-in. dart; 1.6-in. clamp; 7.6 mph; ASTM-D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.8 °C @Thickness 3.17 mm |
190 °F @Thickness 0.125 in |
Unannealed; ASTM-D648 |
| 96.1 °C @Thickness 6.35 mm |
205 °F @Thickness 0.250 in |
Unannealed; ASTM-D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 62.2 °C @Thickness 3.17 mm |
144 °F @Thickness 0.125 in |
Unannealed; ASTM-D648 |
| 72.2 °C @Thickness 6.35 mm |
162 °F @Thickness 0.250 in |
Unannealed; ASTM-D648 | |
| Vicat Softening Point | 170 °C @Load 1.00 kg |
338 °F @Load 2.20 lb |
Rate B, 120°C/hour; ASTM-D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 3.20e+13 ohm | 3.20e+13 ohm | ASTM-D257 |
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz |
3.5 @Frequency 1.00e+6 Hz |
Tinfoil Electrodes; ASTM-D150 |
| Dielectric Strength | 15.0 kV/mm @Thickness 1.57 mm |
380 kV/in @Thickness 0.0620 in |
Short time under oil; ASTM-D149 |
| Dissipation Factor | 0.039 @Frequency 1.00e+6 Hz |
0.039 @Frequency 1.00e+6 Hz |
Tinfoil Electrodes; ASTM-D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Middle Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Front Barrel Temperature | 232 - 266 °C | 450 - 511 °F | Injection Molding |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | Injection Molding |
| Melt Temperature | 238 - 271 °C | 460 - 520 °F | Injection Molding |
| Mold Temperature | 38.0 - 66.0 °C | 100 - 151 °F | Injection Molding |
| Drying Temperature | 88.0 °C @Time 7200 - 14400 sec |
190 °F @Time 2.00 - 4.00 hour |
|
| Moisture Content | 0.15 - 0.35 % | 0.15 - 0.35 % | |
| Dew Point | <= -29.0 °C | <= -20.2 °F | inlet air |
| Injection Pressure | 41.4 - 82.7 MPa | 6000 - 12000 psi | Injection Molding |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | Injection Molding |
| Clamp Pressure | 46.2 - 77.0 MPa | 6700 - 11200 psi | Injection Molding |
| Cushion | <= 0.317 cm | <= 0.125 in | Injection Molding |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Hold Pressure | 30-50% of Injection Pressure, Injection Molding | |
| Injection Speed | Fast | Injection Molding |
| Screw Compression Ratio | 2.5:1 | Injection Molding |
| Screw Length-to-Diameter Ratio | >= 20:1 | Injection Molding |
| Screw Speed | Moderate, Injection Molding | |
| Shot Weight-to-Machine Capacity Ratio | 0.5-0.7 | Injection Molding |
Users viewing this material also viewed the following:
- NCMT NanoPAC™ S201 High Performance Polypropylene Nanocomposite
- Glastic Laminates/Shapes UTR Pultruded Tubing, Fiberglass-Reinforced Polyester
- SABIC Innovative Plastics LNP Thermocomp KB005 Acetal Copolymer
- Teknor Apex Sinpolene MBB2691 Linear Low Density Polyethylene
- ExxonMobil Mobil Delvac 50 1650
- Eagle Brass 19210 XP-10 Copper Iron, Spring
- ChevronTexaco Gear Compounds EP, ISO 1000
- DuPont™ Kapton® 200ZT Polyimide Film, 50 Micron Thickness
- Henkel Hysol EA 9395 Paste Adhesive System
Copyright © lookpolymers.com All Rights Reserved