Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (DAM)
| Category | Polymer , Thermoplastic , ABS Polymer , Nylon |
| Manufacturer | Ineos ABS |
| Trade Name | Triax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Triax® 1315 GF ABS + Polyamide Blend (DAM).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Key Features:Contains FillerSuitable processing methods:Injection molding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.995 g/cc | 0.0359 lb/in³ | Melt |
| 1.17 g/cc | 0.0423 lb/in³ | ||
| Water Absorption | 3.8 % | 3.8 % | |
| Moisture Absorption at Equilibrium | 1.3 % | 1.3 % | 23°C/50% R.H. |
| Linear Mold Shrinkage, Flow | 0.0040 cm/cm | 0.0040 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm | 0.0035 in/in | |
| Melt Flow | 3.0 g/10 min @Load 5.00 kg, Temperature 260 °C |
3.0 g/10 min @Load 11.0 lb, Temperature 500 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 82.0 MPa | 11900 psi | |
| Elongation at Break | 4.0 % | 4.0 % | |
| Tensile Modulus | 4.80 GPa | 696 ksi | |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | |
| 3.60 J/cm² @Temperature -30.0 °C |
17.1 ft-lb/in² @Temperature -22.0 °F |
||
| Charpy Impact, Notched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| 0.600 J/cm² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 40.0 µm/m-°C @Temperature 20.0 °C |
22.2 µin/in-°F @Temperature 68.0 °F |
|
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 20.0 °C |
66.7 µin/in-°F @Temperature 68.0 °F |
|
| Specific Heat Capacity | 1.94 J/g-°C | 0.464 BTU/lb-°F | Melt |
| Thermal Conductivity | 0.155 W/m-K | 1.08 BTU-in/hr-ft²-°F | Melt |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | |
| Vicat Softening Point | 112 °C | 234 °F | 50°C/h 50N |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | |
| Dielectric Constant | 3.8 @Frequency 1e+6 Hz |
3.8 @Frequency 1e+6 Hz |
|
| 4.6 @Frequency 100 Hz |
4.6 @Frequency 100 Hz |
||
| Dielectric Strength | 40.0 kV/mm | 1020 kV/in | |
| Dissipation Factor | 0.028 @Frequency 1e+6 Hz |
0.028 @Frequency 1e+6 Hz |
|
| 0.032 @Frequency 100 Hz |
0.032 @Frequency 100 Hz |
||
| Comparative Tracking Index | 600 V | 600 V |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 260 °C | 500 °F | Injection Molding |
| Mold Temperature | 80.0 °C | 176 °F | Injection Molding |
| Ejection Temperature | 105 °C | 221 °F | |
| Injection Velocity | 40.0 mm/sec | 1.57 in/sec |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Effective thermal diffusivity | 0.801E-7 m²/s | Melt |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P2765 TPE, PP Overmold or Standalone use
- Kinetics MIM 4605 Low Alloy Steel (Austempered)
- Lubriplate SYN SYN-1600 PAO-Based Multi-Purpose Grease
- Schott N-KF9 Glass
- SABIC Innovative Plastics NORYL GTX GTX942 PPE+PS+PA66
- Wieland 1951 Wilaform Platinum
- ConocoPhillips HD Fleet Supreme™ 10W-30 Engine Oil
- Arkema Group Rilsan® BZM 8 NOIR TL Nylon 11, 8% Glass Fiber Filled (Conditioned)
- American Computer Optics Water White Filter 10 mm
- Beijing Chemical Industry KAIFA® 301-G20 PBT Resin
Copyright © lookpolymers.com All Rights Reserved