Sumitomo Bakelite North America E 8354A-1 Short Glass Fiber Reinforced Epoxy
| Category | Polymer , Thermoset , Epoxy , Epoxy, Molded, Glass Fiber Filler , Filled/Reinforced Thermoset |
| Manufacturer | Sumitomo Bakelite North America |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sumitomo Bakelite North America E 8354A-1 Short Glass Fiber Reinforced Epoxy.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
E 8354A-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength.Information provided by Sumitomo Bak North America, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.800 g/cc | 0.0289 lb/in³ | ASTM D1895 |
| Density | 2.04 g/cc | 0.0737 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % @Temperature 50.0 °C, Time 173000 sec |
0.20 % @Temperature 122 °F, Time 48.0 hour |
ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0030 cm/cm | 0.0020 - 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| Flexural Strength | 149 MPa | 21600 psi | at rupture; ASTM D790 |
| Flexural Modulus | 20.0 GPa | 2900 ksi | ASTM D790 |
| Compressive Strength | 260 MPa | 37700 psi | ASTM D695 |
| Izod Impact, Notched | 0.340 J/cm | 0.637 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C | 12.2 µin/in-°F | ASTM E831 |
| Maximum Service Temperature, Air | 130 °C | 266 °F | UL Temperature Index; UL 746B |
| Deflection Temperature at 1.8 MPa (264 psi) | 275 °C | 527 °F | Post Baked; ASTM D648A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 4.4 @Frequency 1.00e+6 Hz |
4.4 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Dielectric Strength | 13.7 kV/mm @Frequency 60.0 Hz |
348 kV/in @Frequency 60.0 Hz |
step-by-step, wet; ASTM D149 |
| 14.8 kV/mm @Frequency 60.0 Hz |
376 kV/in @Frequency 60.0 Hz |
short time, wet; ASTM D149 | |
| Dissipation Factor | 0.015 @Frequency 1.00e+6 Hz |
0.015 @Frequency 1.00e+6 Hz |
wet; ASTM D150 |
| Arc Resistance | 185 sec | 185 sec | ASTM D495 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Form | Granular | |
| Molding Method | Compression | |
| Transfer |
Users viewing this material also viewed the following:
- Shin-Etsu Silicones KE-3490 Silicone, RTV
- Techmer ES HiFill® HDPE GF40 40% Glass Filled
- Teknor Apex Telcar® TL-6045 Thermoplastic Elastomer
- Trelleborg Commercial Neoprene® C800 Chloroprene
- Teknor Apex Telcar® TELC 1025-70 Thermoplastic Elastomer
- Cheng Yu Plastic PP237G2 Polypropylene, 20% Glass Fiber
- CP-Polymer-Technik Wellamid® 6000 S Nylon 6, Finely Crystalline, Conditioned
- Arlon 0.015" (0.381 mm) Flexible Heater Silicone with Fiberglass Substrate (51581R015)
- Polimeri Europa KOBLEND PCA 53 PC+ABS (discontinued **)
Copyright © lookpolymers.com All Rights Reserved