3M Dyneon™ TF 4215 PTFE 25% Electrocarbon Filled (discontinued **)
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Conductive Carbon Filled |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | 3M Dyneon™ TF 4215 PTFE 25% Electrocarbon Filled
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications include bearings, seals/gaskets, packings, piston rings.Data provided by Dyneon.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 g/cc | 0.0762 lb/in³ | Sintered moldings; ASTM D4894/D4895 |
| Apparent Bulk Density | 0.750 g/cc | 0.0271 lb/in³ | DIN 53 466 |
| Linear Mold Shrinkage | 0.023 cm/cm @Thickness 80.0 mm |
0.023 in/in @Thickness 3.15 in |
sheet; ASTM D4894 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | ASTM D2240 |
| Tensile Strength, Ultimate | 16.0 MPa @Thickness 2.00 mm |
2320 psi @Thickness 0.0787 in |
ASTM D4894 |
| Elongation at Break | 180 % @Thickness 2.00 mm |
180 % @Thickness 0.0787 in |
ASTM D4894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 90.0 µm/m-°C @Temperature 30.0 - 100 °C |
50.0 µin/in-°F @Temperature 86.0 - 212 °F |
|
| 100 µm/m-°C @Temperature 30.0 - 200 °C |
55.6 µin/in-°F @Temperature 86.0 - 392 °F |
||
| 120 µm/m-°C @Temperature 30.0 - 300 °C |
66.7 µin/in-°F @Temperature 86.0 - 572 °F |
||
| Thermal Conductivity | 0.600 W/m-K | 4.16 BTU-in/hr-ft²-°F | DIN 52 612 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | IEC 60093 |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PH 51 C 40 Polypropylene Homopolymer and Copolymer, 40% Micronized Talc
- Polimeri Europa Extir® B 2000 Expandable Polystyrene, Fast Molding (discontinued **)
- 3M Dyneon™ CC607 PTFE 35% Fiberglass Filled (discontinued **)
- SABIC Innovative Plastics Ultem DH1004F PEI
- Techmer ES Luriblend® POM CO TL20 Acetal
- Trelleborg Emerson & Cuming Stycast® 5952 Two-Component Easy Mix Ratio Encapsulant
- ExxonMobil 636 Mobilgear 600 Series
- Axiall 8852 Moldings & Extrusions Flexible PVC
- 3M Dyneon™ PFE 191TZ High Temperature Perfluoroelastomer
- Plenco 302 Black Impact Grade Woodflour/Flock Filled Phenolic Molding Compound (discontinued **)
Copyright © lookpolymers.com All Rights Reserved