Ineos ABS Lustran® 456 Extrusion, Matte-Gloss (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ineos ABS Lustran® 456 Extrusion, Matte-Gloss
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ASTM D792 |
| Melt Flow | 1.2 g/10 min @Load 3.80 kg, Temperature 230 °C |
1.2 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 68 | 68 | ASTM D785 |
| Tensile Strength, Yield | 13.0 MPa | 1890 psi | ASTM D638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | ASTM D638 |
| Flexural Yield Strength | 28.3 MPa | 4100 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 1.90 J/cm @Thickness 3.17 mm |
3.56 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| 0.900 J/cm @Thickness 3.17 mm, Temperature -40.0 °C |
1.69 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F |
ASTM D256 | |
| Impact Test | 38.0 J @Thickness 2.50 mm |
28.0 ft-lb @Thickness 0.0984 in |
Instrumented Impact, Total Energy; 2.5 mm thick, 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 95.0 µm/m-°C @Temperature 20.0 °C |
52.8 µin/in-°F @Temperature 68.0 °F |
Injection molded sample; ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 89.0 °C @Thickness 3.17 mm |
192 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C @Thickness 3.17 mm |
176 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| UL RTI, Electrical | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical with Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| UL RTI, Mechanical without Impact | 60.0 °C @Thickness 1.60 mm |
140 °F @Thickness 0.0630 in |
UL746B |
| Flammability, UL94 | HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
|
| HB @Thickness 1.47 mm |
HB @Thickness 0.0579 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | <= 10 % | <= 10 % | 60°; Sheet; ASTM D523 |
| Transmission, Visible | 0.00 % | 0.00 % | Opaque only |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 215 - 240 °C | 419 - 464 °F |
Users viewing this material also viewed the following:
- LyondellBasell Petrothene® GA574189 Linear Low Density Polyethylene, Injection Molding Grade
- Materion BrushBronze® 95510 (AMS 4880) Continuous Cast 0.250" - 4.0"
- Lucite International Diakon® Rapide CLG 910B Enhanced Molding Acrylic Polymer
- SABIC Innovative Plastics NORYL V090 PPE+HIPS (Europe-Africa-Middle East)
- Chase Plastics CP Pryme® NN100M2 (Dry) Nylon 66, Lubricated
- Eagle Brass 151 ZHC® COPPER, Hard
- Eagle Brass 752 Nickel Silver 18%, Annealed
- Arkema Group Pebax® 4033 SA 01 Polyether Block Amide (PEBA)
- Bisalloy Steels BisPlate 80 Thickness >80-100 mm
- LNP Thermocomp® JF-1006 EM Polyethersulfone, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved