ExxonMobil PP7054L1 Polypropylene Impact Copolymer

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Impact Modified; Molded/Extruded
Manufacturer	Exxon Chemical
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil PP7054L1 Polypropylene Impact Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A nucleated impact copolymer resin with medium flow. It is suitable for molding applications like consumer products, closures, containers, toys and rigid packaging applications.Availability: Africa & Middle East and Europe Features:Good Flow Nucleated Uses: Battery CasesConstruction ApplicationsContainers CratesIndustrial ApplicationsPailsRigid PackagingTool/Tote BoxToysProcessing Method: Injection Molding and CompoundingInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ExxonMobil Method
Melt Flow	17 g/10 min @Load 2.16 kg, Temperature 230 °C	17 g/10 min @Load 4.76 lb, Temperature 446 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Hardness, Shore D	62	62	ISO 868
Tensile Strength, Yield	23.0 MPa	3340 psi	ISO 527-2/50
Elongation at Yield	4.0 %	4.0 %	ISO 527-2/50
Tensile Modulus	1.25 GPa	181 ksi	Secant; ISO527-2/1
Flexural Modulus	1.10 GPa	160 ksi	ISO 178
Izod Impact, Notched (ISO)	7.98 kJ/m²	3.80 ft-lb/in²	ISO 180/1A
Charpy Impact, Notched	0.504 J/cm² @Temperature -20.0 °C	2.40 ft-lb/in² @Temperature -4.00 °F	ISO 179/1eA
	0.693 J/cm² @Temperature 0.000 °C	3.30 ft-lb/in² @Temperature 32.0 °F	ISO 179/1eA
	1.09 J/cm² @Temperature 22.8 °C	5.20 ft-lb/in² @Temperature 73.0 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	324 °C	615 °F	ISO 3146
Crystallization Temperature	252 °C	486 °F	ISO 3146
Deflection Temperature at 0.46 MPa (66 psi)	87.8 °C	190 °F	ISO 75-2/B
Deflection Temperature at 1.8 MPa (264 psi)	51.1 °C	124 °F	ISO 75-2/A
Vicat Softening Point	146 °C	295 °F	ISO 306/A50