Ineos ABS Lustran® 256 Extrusion, Blending  (discontinued **)

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Extruded
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Ineos ABS Lustran® 256 Extrusion, Blending  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A natural, medium-flow, medium-impact extrusion grade of ABS. It is used for blending with other Lustran ABS virgin and regrind materials to optimize cost and performance.Properties tested in transverse direction (worst case) on 125-mil (3.2 mm) extruded sheets specimens with
Physical Properties Metric English Comments
Density 1.05 g/cc
0.0379 lb/in³
ASTM D792
Melt Flow 14 g/10 min

@Load 10.0 kg,
Temperature 230 °C
14 g/10 min

@Load 22.0 lb,
Temperature 446 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 40.0 MPa
5800 psi
ASTM D638
Tensile Modulus 2.20 GPa
319 ksi
ASTM D638
Flexural Yield Strength 69.0 MPa
10000 psi
ASTM D790
Flexural Modulus 2.40 GPa
348 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm

@Thickness 3.17 mm
3.00 ft-lb/in

@Thickness 0.125 in
ASTM D256
0.480 J/cm

@Thickness 3.17 mm,
Temperature -40.0 °C
0.899 ft-lb/in

@Thickness 0.125 in,
Temperature -40.0 °F
ASTM D256
Impact Test 30.0 J

@Thickness 2.50 mm
22.1 ft-lb

@Thickness 0.0984 in
Instrumented Impact, Total Energy; 7.6 mph, 3 in. clamp, 0.5 in. dart; ASTM D3763
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 87.0 °C

@Thickness 3.17 mm
189 °F

@Thickness 0.125 in
Unannealed; ASTM D648
UL RTI, Electrical 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical with Impact 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
UL RTI, Mechanical without Impact 60.0 °C

@Thickness 1.60 mm
140 °F

@Thickness 0.0630 in
UL746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Natural color
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
Natural color
Optical Properties Metric English Comments
Gloss 90 %
90 %
60°; Sheet; ASTM D523
Transmission, Visible 0.00 %
0.00 %
Opaque only
Processing Properties Metric English Comments
Melt Temperature 215 - 240 °C
419 - 464 °F