IRPC Polimaxx Polene HI830 Polystyrene

Category Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced
Manufacturer IRPC Polimaxx
Trade Name Polene
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF IRPC Polimaxx Polene HI830 Polystyrene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
APPLICATIONS: EXTRUSION APPLICATION, VACUUM SHEET : FOOD PACKAGING ELECTRICAL APPLIANCES, HOUSEHOLD PRODUCT, TOYS, SANITARY, etc.
Physical Properties Metric English Comments
Melt Flow 3.0 g/10 min

@Load 5.00 kg,
Temperature 200 °C
 3.0 g/10 min

@Load 11.0 lb,
Temperature 392 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell L 82

@Thickness 6.35 mm,
Temperature 23.0 °C
 82

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D785
Tensile Strength, Yield 21.4 MPa

@Temperature 23.0 °C
 3100 psi

@Temperature 73.4 °F
 ASTM D638
Flexural Yield Strength 41.4 MPa

@Temperature 23.0 °C
 6000 psi

@Temperature 73.4 °F
 ASTM D790
Flexural Modulus 2.14 GPa

@Temperature 23.0 °C
 310 ksi

@Temperature 73.4 °F
 ASTM D790
Izod Impact, Notched 0.120 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
 0.225 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 90.0 °C

@Thickness 6.35 mm
 194 °F

@Thickness 0.250 in
 ASTM D648
Vicat Softening Point 96.0 °C

@Load 1.00 kg,
Thickness 3.17 mm
 205 °F

@Load 2.20 lb,
Thickness 0.125 in
 ASTM D1525
Flammability, UL94 HB

@Thickness 3.00 mm
 HB

@Thickness 0.118 in
Processing Properties Metric English Comments
Processing Temperature 190 - 230 °C
374 - 446 °F
extrusion
Drying Temperature 80.0 - 85.0 °C

@Time 7200 - 10800 sec
 176 - 185 °F

@Time 2.00 - 3.00 hour