Huntsman IROGRAN® A 92 P 4207 TPU-Polyether
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyurethane TPE , Polyurethane, TP , Thermoplastic Polyurethane, Elastomer, Ether Grade |
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Huntsman IROGRAN® A 92 P 4207 TPU-Polyether.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Excellent resistance to hydrolysis and microbial attack. Suggested for injection molding and extrusion.Information provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM D995 |
| Melt Flow | 15 - 30 g/10 min | 15 - 30 g/10 min | Melt Volume Rate (cm³/10 min) |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 92 | 92 | ASTM D2240 |
| Hardness, Shore D | 40 | 40 | ASTM D2240 |
| Tensile Strength at Break | 49.0 MPa | 7110 psi | DIN 53504 |
| Elongation at Break | 640 % | 640 % | ASTM D412 |
| 100% Modulus | 0.00950 GPa | 1.38 ksi | DIN 53504 |
| 300% Modulus | 0.0166 GPa | 2.41 ksi | DIN 53504 |
| Rebound | 34 % | 34 % | Bayshore; ASTM D2632 |
| Tear Strength | 119 kN/m | 680 pli | ASTM D624 |
| Abrasion | 25 | 25 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 28 % @Temperature 23.0 °C, Time 252000 sec |
28 % @Temperature 73.4 °F, Time 70.0 hour |
ASTM D395 |
| 44 % @Temperature 70.0 °C, Time 86400 sec |
44 % @Temperature 158 °F, Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 165 - 188 °C | 329 - 370 °F | Huntsman/TMA |
Users viewing this material also viewed the following:
- Polyplastic TechnoTep B® 45 D Thermoplastic Elastomer, Mineral Filled
- SABIC Innovative Plastics Lexan® EXL1414 PC Copolymer (Europe-Africa-Middle East)
- Hyosung Topilene R530A PP
- Garlock 8316 EPDM Sheet Rubber Gasketing
- SGL Carbon Group EK 203 Graphite
- Samsung Cheil Industries Infino® TK-6036H PPA, Glass Filled
- A. Schulman POLYBATCH™ Green P30244/4 Concentrate Based In Copolymer PP
- CP-Polymer-Technik Wellamid® 6600 GV 40 HWCP 40% Glass Fiber Nylon 66, Heat Stabilized, Dry
- Ametek P304L P/M Stainless Steel, Sintered from 6.25 g/cc Green Density
- Lushan EV1050G2 EVA Film for Encapsulating Solar modules, High Transmittance
Copyright © lookpolymers.com All Rights Reserved