Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet

Category Metal , Nonferrous Metal , Nickel Alloy , Superalloy
Manufacturer Haynes International, Inc.
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Haynes 230® alloy, cold rolled and 1232°C solution annealed sheet.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Excellent high-temperature strength, outstanding resistance to oxidizing environments up to 1149°C, premier resistance to nitriding environments, and excellent long-term thermal stability. Applications include combustion cans, transition ducts, flameholders, thermocouple sheaths and other gas turbine components; used for catalyst grid supports in ammonia burners, high-strength thermocouple protection tubes, high-temperature heat exchangers, ducts, high-temperature bellows; furnace retorts, chains and fixtures, burner flame shrouds, recuperator internals, dampers, nitriding furnace internals, heat-treating baskets, grates, trays, sparger tubes, and cyclone internals.Data provided by the manufacturer, Haynes International, Inc.
Physical Properties Metric English Comments
Density 8.97 g/cc
0.324 lb/in³
at RT
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 860 MPa
125000 psi
55.0 MPa

@Temperature 1204 °C
 7980 psi

@Temperature 2199 °F
79.0 MPa

@Temperature 1149 °C
 11500 psi

@Temperature 2100 °F
120 MPa

@Temperature 1093 °C
 17400 psi

@Temperature 1999 °F
225 MPa

@Temperature 982 °C
 32600 psi

@Temperature 1800 °F
400 MPa

@Temperature 871 °C
 58000 psi

@Temperature 1600 °F
585 MPa

@Temperature 760 °C
 84800 psi

@Temperature 1400 °F
670 MPa

@Temperature 649 °C
 97200 psi

@Temperature 1200 °F
710 MPa

@Temperature 538 °C
 103000 psi

@Temperature 1000 °F
Tensile Strength, Yield 390 MPa

@Strain 0.200 %
 56600 psi

@Strain 0.200 %
26.0 MPa

@Strain 0.200 %,
Temperature 1204 °C
 3770 psi

@Strain 0.200 %,
Temperature 2199 °F
39.0 MPa

@Strain 0.200 %,
Temperature 1149 °C
 5660 psi

@Strain 0.200 %,
Temperature 2100 °F
57.0 MPa

@Strain 0.200 %,
Temperature 1093 °C
 8270 psi

@Strain 0.200 %,
Temperature 1999 °F
120 MPa

@Strain 0.200 %,
Temperature 982 °C
 17400 psi

@Strain 0.200 %,
Temperature 1800 °F
225 MPa

@Strain 0.200 %,
Temperature 871 °C
 32600 psi

@Strain 0.200 %,
Temperature 1600 °F
270 MPa

@Strain 0.200 %,
Temperature 649 °C
 39200 psi

@Strain 0.200 %,
Temperature 1200 °F
275 MPa

@Strain 0.200 %,
Temperature 538 °C
 39900 psi

@Strain 0.200 %,
Temperature 1000 °F
285 MPa

@Strain 0.200 %,
Temperature 760 °C
 41300 psi

@Strain 0.200 %,
Temperature 1400 °F
Elongation at Break 47.7 %
47.7 %
in 50.8 mm
31.2 %

@Temperature 1204 °C
 31.2 %

@Temperature 2199 °F
 in 50.8 mm
39.5 %

@Temperature 1149 °C
 39.5 %

@Temperature 2100 °F
 in 50.8 mm
46.1 %

@Temperature 760 °C
 46.1 %

@Temperature 1400 °F
 in 50.8 mm
49.6 %

@Temperature 1093 °C
 49.6 %

@Temperature 1999 °F
 in 50.8 mm
55 %

@Temperature 649 °C
 55 %

@Temperature 1200 °F
 in 50.8 mm
55.7 %

@Temperature 538 °C
 55.7 %

@Temperature 1000 °F
 in 50.8 mm
58.9 %

@Temperature 871 °C
 58.9 %

@Temperature 1600 °F
 in 50.8 mm
70.5 %

@Temperature 982 °C
 70.5 %

@Temperature 1800 °F
 in 50.8 mm
Modulus of Elasticity 211 GPa
30600 ksi
RT
150 GPa

@Temperature 1000 °C
 21800 ksi

@Temperature 1830 °F
157 GPa

@Temperature 900 °C
 22800 ksi

@Temperature 1650 °F
164 GPa

@Temperature 800 °C
 23800 ksi

@Temperature 1470 °F
171 GPa

@Temperature 700 °C
 24800 ksi

@Temperature 1290 °F
177 GPa

@Temperature 600 °C
 25700 ksi

@Temperature 1110 °F
184 GPa

@Temperature 500 °C
 26700 ksi

@Temperature 932 °F
190 GPa

@Temperature 400 °C
 27600 ksi

@Temperature 752 °F
196 GPa

@Temperature 300 °C
 28400 ksi

@Temperature 572 °F
202 GPa

@Temperature 200 °C
 29300 ksi

@Temperature 392 °F
207 GPa

@Temperature 100 °C
 30000 ksi

@Temperature 212 °F
Charpy Impact 73.0 J
53.8 ft-lb
solution annealed (unknown temp)
Thermal Properties Metric English Comments
CTE, linear 12.7 µm/m-°C

@Temperature 25.0 - 100 °C
 7.06 µin/in-°F

@Temperature 77.0 - 212 °F
13.0 µm/m-°C

@Temperature 25.0 - 200 °C
 7.22 µin/in-°F

@Temperature 77.0 - 392 °F
13.3 µm/m-°C

@Temperature 25.0 - 300 °C
 7.39 µin/in-°F

@Temperature 77.0 - 572 °F
13.7 µm/m-°C

@Temperature 25.0 - 400 °C
 7.61 µin/in-°F

@Temperature 77.0 - 752 °F
14.0 µm/m-°C

@Temperature 25.0 - 500 °C
 7.78 µin/in-°F

@Temperature 77.0 - 932 °F
14.4 µm/m-°C

@Temperature 25.0 - 600 °C
 8.00 µin/in-°F

@Temperature 77.0 - 1110 °F
14.8 µm/m-°C

@Temperature 25.0 - 700 °C
 8.22 µin/in-°F

@Temperature 77.0 - 1290 °F
15.2 µm/m-°C

@Temperature 25.0 - 800 °C
 8.44 µin/in-°F

@Temperature 77.0 - 1470 °F
15.7 µm/m-°C

@Temperature 25.0 - 900 °C
 8.72 µin/in-°F

@Temperature 77.0 - 1650 °F
16.1 µm/m-°C

@Temperature 25.0 - 1000 °C
 8.94 µin/in-°F

@Temperature 77.0 - 1830 °F
Specific Heat Capacity 0.397 J/g-°C
0.0949 BTU/lb-°F
RT
0.419 J/g-°C

@Temperature 100 °C
 0.100 BTU/lb-°F

@Temperature 212 °F
0.435 J/g-°C

@Temperature 200 °C
 0.104 BTU/lb-°F

@Temperature 392 °F
0.448 J/g-°C

@Temperature 300 °C
 0.107 BTU/lb-°F

@Temperature 572 °F
0.465 J/g-°C

@Temperature 400 °C
 0.111 BTU/lb-°F

@Temperature 752 °F
0.473 J/g-°C

@Temperature 500 °C
 0.113 BTU/lb-°F

@Temperature 932 °F
0.486 J/g-°C

@Temperature 600 °C
 0.116 BTU/lb-°F

@Temperature 1110 °F
0.574 J/g-°C

@Temperature 700 °C
 0.137 BTU/lb-°F

@Temperature 1290 °F
Electrical Properties Metric English Comments
Electrical Resistivity 0.000125 ohm-cm
0.000125 ohm-cm
RT
0.000125 ohm-cm

@Temperature 1000 °C
 0.000125 ohm-cm

@Temperature 1830 °F
0.0001258 ohm-cm

@Temperature 100 °C
 0.0001258 ohm-cm

@Temperature 212 °F
0.0001265 ohm-cm

@Temperature 200 °C
 0.0001265 ohm-cm

@Temperature 392 °F
0.0001271 ohm-cm

@Temperature 900 °C
 0.0001271 ohm-cm

@Temperature 1650 °F
0.0001273 ohm-cm

@Temperature 300 °C
 0.0001273 ohm-cm

@Temperature 572 °F
0.0001284 ohm-cm

@Temperature 400 °C
 0.0001284 ohm-cm

@Temperature 752 °F
0.0001291 ohm-cm

@Temperature 800 °C
 0.0001291 ohm-cm

@Temperature 1470 °F
0.0001302 ohm-cm

@Temperature 500 °C
 0.0001302 ohm-cm

@Temperature 932 °F
0.0001307 ohm-cm

@Temperature 700 °C
 0.0001307 ohm-cm

@Temperature 1290 °F
0.0001312 ohm-cm

@Temperature 600 °C
 0.0001312 ohm-cm

@Temperature 1110 °F
Users viewing this material also viewed the following: