Grupo Repol Dinalon® B1S25 G25XV0 PA6 25% Glass Fiber V0
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® B1S25 G25XV0 PA6 25% Glass Fiber V0.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties for Dry As Molded samplesInformation provided by Grupo Repol
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.50 g/cc | 0.0542 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 160 MPa | 23200 psi | ISO 527 |
| Elongation at Break | 2.7 % | 2.7 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 200 MPa | 29000 psi | ISO 178 |
| Flexural Modulus | 7.20 GPa | 1040 ksi | ISO 178 |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | 1.00 J/cm² @Temperature 23.0 °C |
4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75/A |
| Vicat Softening Point | >= 200 °C | >= 392 °F | 50N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C | 1760 °F | UNE-EN 60695 |
Users viewing this material also viewed the following:
- Network Polymers Kepital® F40-03
- Overview of materials for ABS/Polyester Alloy
- TSE Industries Millathane® E34 Millable Polyether Polyurethane Rubber with TP-95
- Teknor Apex Sinvicomp SFW 6500 Polyvinyl Chloride, Flexible
- Plenco 08112 Polyester BMC, Compression Molded
- Zircar Refractory Composites SB-2000 SILICA BLANKET
- Clariant Renol PA1SP0004 Nylon 66, High Impact Modified, ESD
- Aclo Accutech Polypropylene Homopolymer HP0336C10L1 Calcium Reinforced
- 3M 5490 PTFE Extruded Film Tape
- Parker Chomerics CHO-MUTE 9005 Microwave Absorber
Copyright © lookpolymers.com All Rights Reserved