Category | Polymer , Thermoset , Polyester, TS , Thermoset Polyester Glass Filled BMC |
Manufacturer | Menzolit |
Trade Name | Menzolit® |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | Menzolit Menzolit® BMC 1650 Unsaturated Polyester UP.pdf ![]() |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Density | 1.90 g/cc | 0.0686 lb/in³ | ISO 1183 |
Water Absorption | <= 0.50 % | <= 0.50 % | ISO 62 |
Linear Mold Shrinkage | 0.00080 cm/cm | 0.00080 in/in | ISO 2577 |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Tensile Strength, Ultimate | 31.0 MPa @Temperature 22.0 °C |
4500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Tensile Strength, Yield | 31.0 MPa @Temperature 22.0 °C |
4500 psi @Temperature 71.6 °F |
25mm flat samples, compression moulded; ISO 527-4 |
Elongation at Yield | 0.00 % | 0.00 % | tensile rupture strain; ISO 527-4 |
Modulus of Elasticity | 13.0 GPa | 1890 ksi | 25mm flat samples, compression moulded; ISO 527-4 |
Flexural Strength | 101 MPa @Temperature 22.0 °C |
14600 psi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Flexural Modulus | 10.0 GPa @Temperature 22.0 °C |
1450 ksi @Temperature 71.6 °F |
25 mm wide 100 mm long, flat samples; ISO 14125 |
Poissons Ratio | 0.30 | 0.30 | |
Shear Modulus | 5.00 GPa | 725 ksi | in plane |
Charpy Impact, Notched | 2.90 J/cm² | 13.8 ft-lb/in² | ISO 179 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
CTE, linear | 10.0 µm/m-°C | 5.56 µin/in-°F | ISO 11359-2 |
Specific Heat Capacity | 1.10 J/g-°C | 0.263 BTU/lb-°F | |
Thermal Conductivity | 0.700 W/m-K | 4.86 BTU-in/hr-ft²-°F | |
Maximum Service Temperature, Air | 165 °C | 329 °F | |
Deflection Temperature at 1.8 MPa (264 psi) | >= 150 °C | >= 302 °F | ISO 75-2 |
Minimum Service Temperature, Air | -40.0 °C | -40.0 °F | |
Glass Transition Temp, Tg | 170 °C | 338 °F | ISO 11357-2 |
Flammability, UL94 | HB @Thickness 3.00 mm |
HB @Thickness 0.118 in |
|
Oxygen Index | 22 % | 22 % | ISO 4589-2 |
Glow Wire Test | 750 °C | 1380 °F | IEC 60695-2-12 |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 |
Dielectric Constant | 4.0 | 4.0 | IEC 60250 |
Dielectric Strength | 30.0 kV/mm | 762 kV/in | IEC 60243-1 |
Dissipation Factor | 0.010 | 0.010 | IEC 60250 |
Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 135 - 150 °C | 275 - 302 °F | Injection moulding, matched metal die |