- Grupo Repol Dinalon® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66
Grupo Repol Dinalon® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Grupo Repol |
| Trade Name | Dinalon® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Grupo Repol Dinalon® A1S25 G25PV0 25% Glass Reinforced, V-0 Rated (Phosphorous) Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Mechanical properties are for dry as molded samples.Information provided by Grupo Repol.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183/A |
| Moisture Absorption at Equilibrium | <= 0.25 % | <= 0.25 % | Karl-Fischer; ISO 15512/A |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 140 MPa | 20300 psi | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Flexural Strength | 180 MPa | 26100 psi | ISO 178 |
| Flexural Modulus | 6.50 GPa | 943 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature 23.0 °C |
3.33 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Charpy Impact Unnotched | 4.00 J/cm² @Temperature 23.0 °C |
19.0 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eU |
| Charpy Impact, Notched | >= 1.00 J/cm² @Temperature 23.0 °C |
>= 4.76 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F | ISO 75/A |
| Vicat Softening Point | >= 230 °C | >= 446 °F | 50 N; ISO 306 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| Glow Wire Test | 960 °C | 1760 °F | IEC 695 |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 2005 XRC Black 20% Filler Content Polypropylene
- Plansee W-10Cu Tungsten-Copper Composite
- Lucas-Milhaupt Black Flux Silver Brazing Flux
- SABIC Innovative Plastics Ultem CRS5211 PEI (Asia Pacific)
- A. Schulman LP390-01 Narrow Molecular Weight Copolymer
- ExxonMobil Jayflex™ MB10 Plasticizer (European Grade)
- 3M FM032 Indoor UL Recognized Clear Polyester Label Products
Copyright © lookpolymers.com All Rights Reserved