Gromax CFG30-SN31N1 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax CFG30-SN31N1 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.36 g/cc | 1.36 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 82 | 82 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 163 MPa | 23600 psi | 50 mm/min; ISO 527 |
| Elongation at Break | 3.4 % | 3.4 % | 50 mm/min; ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 7.65 GPa | 1110 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 12.6 kJ/m² | 6.00 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 6.00 J/cm² @Temperature 23.0 °C |
28.6 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.32 J/cm² @Temperature 23.0 °C |
6.28 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 240 °C | 464 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 266 - 280 °C | 511 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Plenco 4759 Phenolic, Granular, Injection Molded (discontinued **)
- Lucobit Lucobatch® 1850 T10 Polyolefin TPO Granules
- Multibase Multi-Flex® A 4001 LC Black TPE Thermoplastic Elastomer
- Sharadaa Ceramics REFINSUL ZAP-019 Insulating Castables
- Samsung Cheil Industries Starex® SD-0150GP High Impact Grade ABS
- Goodfellow Carbon/Vinyl Ester Rod
- Lubrizol ESTANE® 5707F1 Ester Based Thermoplastic Polyurethane (European Grade)
- Braskem IA59U3 HDPE Injection Molding Polyethylene Homopolymer
- BASF Novolen® 1102 G Polypropylene
- Solvay Specialty Polymers Amodel® A-4133 L Polyphthalamide (PPA), Dry (discontinued **)
Copyright © lookpolymers.com All Rights Reserved