Gromax CCP PET 9130-104 30% Glass Filled

Category Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 30% Glass Reinforced
Manufacturer Gromax
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Gromax CCP PET 9130-104 30% Glass Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Product Description: PET glass/mineral 30% reinforced injection molding grade. Characteristics:Excellent electrical property Excellent mechanic and chemical property Excellent weatherability Excellent wear property Excellent moldability High resistance to fuels, oil, fats and many solventsLow warp ageInformation provided by Gromax Enterprises Corp.
Physical Properties Metric English Comments
Specific Gravity 1.70 g/cc
1.70 g/cc
ASTM D792
Moisture Absorption 0.0500 %

@Time 86400 sec
0.0500 %

@Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0010 - 0.0030 cm/cm

@Thickness 1.60 mm
0.0010 - 0.0030 in/in

@Thickness 0.0630 in
horizontal; ASTM D955
0.0040 - 0.011 cm/cm

@Thickness 1.60 mm
0.0040 - 0.011 in/in

@Thickness 0.0630 in
vertical; ASTM D955
Mechanical Properties Metric English Comments
Tensile Strength 125.0 MPa
18130 psi
ASTM D638
Elongation at Break 3.0 %
3.0 %
ASTM D638
Flexural Strength 195 MPa
28300 psi
ASTM D790
Flexural Modulus 9.81 GPa
1420 ksi
ASTM D790
Izod Impact, Notched >= 0.883 J/cm

@Thickness 6.35 mm
>= 1.65 ft-lb/in

@Thickness 0.250 in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 20.0 µm/m-°C
11.1 µin/in-°F
ASTM D696
Melting Point 255 °C
491 °F
DSC
Deflection Temperature at 0.46 MPa (66 psi) 247 °C
477 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 227 °C
441 °F
ASTM D648
Flammability, UL94 V-0

@Thickness 0.800 mm
V-0

@Thickness 0.0315 in
Electrical Properties Metric English Comments
Volume Resistivity 1.00e+15 ohm-cm
1.00e+15 ohm-cm
ASTM D257
Surface Resistance 1.00e+13 ohm
1.00e+13 ohm
ASTM D257
Dielectric Constant 3.8

@Frequency 60.0 Hz
3.8

@Frequency 60.0 Hz
ASTM D150
Dielectric Strength 22.0 kV/mm

@Thickness 2.00 mm
559 kV/in

@Thickness 0.0787 in
ASTM D149
Dissipation Factor 0.011

@Frequency 60.0 Hz
0.011

@Frequency 60.0 Hz
ASTM D150
Arc Resistance 100 sec
100 sec
ASTM D495
Processing Properties Metric English Comments
Processing Temperature 250 - 270 °C
482 - 518 °F
Nozzle Temperature 260 - 280 °C
500 - 536 °F
Mold Temperature 80.0 - 140 °C
176 - 284 °F
suitable temperature 90-120°C
Injection Pressure 50.0 - 120 MPa
7250 - 17400 psi
Hold Pressure 30.0 - 80.0 MPa
4350 - 11600 psi
Back Pressure 0.000 - 0.300 MPa
0.000 - 43.5 psi
Screw Speed 100 - 200 rpm
100 - 200 rpm
to be chosen in such a way that plasticizing time is just within cooling time
Descriptive Properties Value Comments
Injection Rate middle-fast