Gromax BTE70-DN001N1 Nylon 6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BTE70-DN001N1 Nylon 6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ISO 1183 |
| Moisture Absorption | 1.80 % | 1.80 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.018 cm/cm | 0.018 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.019 cm/cm | 0.019 in/in | 60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 66 | 66 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 41.2 MPa | 5970 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 80 % | 80 % | 50 mm/min; ISO 527 |
| Flexural Strength | 68.0 MPa | 9860 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.57 GPa | 228 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched | >= NB | >= NB | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 69.0 kJ/m² | 32.8 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.90 J/cm² @Temperature -30.0 °C |
9.04 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 7.40 J/cm² @Temperature 23.0 °C |
35.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Ineos Nova Zyntar® F7120 Developmental Flame Retardant Polystyrene (discontinued **)
- Lehmann & Voss LUVOCOM® 1850-7854 PBT, with carbon fiber and glass fiber
- Flint Hills P5M4K-046 Random Copolymer Polypropylene
- Solvay MACKAZOLINE® O-V Surfactant
- Teknor Apex Sinvicomp SIG 5062 Polyvinyl Chloride, Flexible
- ExxonMobil Mobil Rarus 824
- Azdel SuperLite® SL550800-100 PP Resin Matrix / 55% Glass Fiber (1 mm Molded Thickness)
- BCC Products BC 7136 Epoxy Casting
- Techmer Lehvoss Compounds Luvotech™ J-4/30/V0 BK2989 PA6/12 (discontinued **)
- Polyram PlusTek RA320G5 Nylon 66 for Injection Molding, 25% Glass-Fiber Reinforced, Flame Retardant and High Stiffness
Copyright © lookpolymers.com All Rights Reserved