Henkel Hysol EA 9396 Paste Adhesive System
| Category | Polymer , Adhesive , Thermoset , Epoxy , Epoxy Adhesive |
| Manufacturer | Henkel |
| Trade Name | Hysol |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Henkel Hysol EA 9396 Paste Adhesive System.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Two-part, low viscosity, unfilled version of Hysol EA 9394. Qualified to BMS 8-301.Applications: Structural Repair Low Viscosity Wet Lay-Up Composite Bonding
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Storage Temperature | 25.0 °C | 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 55.2 MPa | 8010 psi | |
| Elongation at Break | 3.4 % | 3.4 % | |
| Tensile Modulus | 2.75 GPa | 399 ksi | |
| Compressive Strength | 482.8 MPa | 70020 psi | Longitudinal compressive strength as a wet lay-up resin with T-300-W133 fiber. |
| Compressive Modulus | 55.15 GPa | 7999 ksi | Longitudinal compressive strength as a wet lay-up resin with T-300-W133 fiber. |
| Adhesive Bond Strength | 22.1 MPa @Temperature 93.0 °C |
3210 psi @Temperature 199 °F |
Tensile Lap Shear |
| 22.8 MPa @Temperature -55.0 °C |
3310 psi @Temperature -67.0 °F |
Tensile Lap Shear | |
| 24.1 MPa @Temperature 25.0 °C |
3500 psi @Temperature 77.0 °F |
Tensile Lap Shear | |
| Peel Strength | 4.40 kN/m | 25.1 pli | Bell Peel |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 177 °C | 351 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min @Temperature 66.0 °C |
1.00 hour @Temperature 151 °F |
|
| 7200 - 10100 min @Temperature 25.0 °C |
120 - 168 hour @Temperature 77.0 °F |
||
| Pot Life | 75 min | 75 min |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Consistency | Low Viscosity | |
| Form | 2 parts | |
| Mix Ratio, Part A:Part B | 100:30 | |
| Peel Strength | Moderate |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL1162T PC Copolymer (Europe-Africa-Middle East)
- Eastman Aqua 18696 PET (discontinued **)
- Sharadaa Ceramics VELECRETE RC 105 Rodding Castables
- Elastomer Engineering E850-85A Polyurethane
- DuPont Teijin Films Melinex® 453 Polyester Film, 142 Gauge
- Ascend Performance Materials Vydyne® R515 Nylon 66, 15% Glass Reinforced, DAM
- SABIC Innovative Plastics LNP THERMOTUF MX00619 PP (Asia Pacific)
- Total Finathene® WR 201 B HDPE blow molding (discontinued **)
Copyright © lookpolymers.com All Rights Reserved