Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-FH00N1 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Melt Flow | 22 g/10 min @Load 5.00 kg, Temperature 275 °C |
22 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 93 | 93 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 183 MPa | 26600 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 3.3 % | 3.3 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 9.80 GPa | 1420 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 275 MPa | 39900 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.58 GPa | 1240 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.5 kJ/m² @Temperature -30.0 °C |
5.00 ft-lb/in² @Temperature -22.0 °F |
ISO 180-1A |
| 15.5 kJ/m² @Temperature 23.0 °C |
7.38 ft-lb/in² @Temperature 73.4 °F |
ISO 180-1A | |
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C |
40.4 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1eU |
| 10.2 J/cm² @Temperature 23.0 °C |
48.5 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU | |
| Charpy Impact, Notched | 1.07 J/cm² @Temperature -30.0 °C |
5.09 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 1.62 J/cm² @Temperature 23.0 °C |
7.71 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 212 °C | 414 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 222 °C | 432 °F | ISO 75-1,-2 |
| Deflection Temperature at 8.0 MPa | 187 °C | 369 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Total Evatane® 28 - 05 HDPE vinyl acetate copolymer, blown film, injection molding (discontinued **)
- Suzhou Hipro Polymers Hiprolon® 11 PFB Colorized Nylon powder
- TSE Industries Millathane® 5004 Millable Polyurethane Elastomer with 20 PHR HAF Black (Typical)
- ExxonMobil Exceed™ 2018CA Metallocene Polyethylene Resin (European Grade)
- Epoxyset Epoxiohm EO-21 Electrically Conductive Epoxy Adhesive
- CIMBAR EliteTalc® 23 Cosmetic Talc
- DuPont Performance Polymers Hytrel® G4074 Polyester Elastomer TPC-ET (Unverified Data**)
- 3M 7732FL Polyester Overlaminating Film
- 3M FV01463 Soft Clear Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved