Gromax BFG30-AH00B3 Nylon 6 30% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 30% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG30-AH00B3 Nylon 6 30% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.35 g/cc | 1.35 g/cc | ISO 1183 |
| Moisture Absorption | 0.900 % | 0.900 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Temperature 80.0 °C |
0.0030 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Melt Flow | 51 g/10 min @Load 5.00 kg, Temperature 275 °C |
51 g/10 min @Load 11.0 lb, Temperature 527 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 91 | 91 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 168.2 MPa | 24390 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 2.8 % | 2.8 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 9.55 GPa | 1390 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 273.4 MPa | 39650 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 8.34 GPa | 1210 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 10.7 kJ/m² | 5.09 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 7.40 J/cm² @Temperature 23.0 °C |
35.2 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 1.08 J/cm² @Temperature 23.0 °C |
5.14 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 215.4 °C | 419.7 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203.1 °C | 397.6 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 1012 C Polypropylene
- Polimeri Europa Europrene Latice® 5585 Carboxylated Styrene - Butadiene Copolymer
- PolyOne Elastamax™ EG-9165 Thermoplastic Elastomer (TPE)
- Teknor Apex Sinpolene MBW1182 Low Density Polyethylene
- Tra-Con Tra-Bond 642-1 Epoxy Adhesive
- EMS-Grivory Grivory® XE 4106 nat PA612-GF30
- ExxonMobil LL 5100.09 Compounding Resin
- Arlon 920-15Rxx-P1 0.020" (0.508 mm) Self-Fusing Silicone Tape
- Gwent Electronic Materials D2090130P5 Pink Dielectric Ink
Copyright © lookpolymers.com All Rights Reserved