SABIC Innovative Plastics LNP THERMOCOMP DC0041PQ PC
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP THERMOCOMP DC0041PQ PC.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* DC0041PQ is a compound based on Polycarbonate resin containing Carbon Fiber. Added feature of this grade is: Flame Retardant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm @Time 86400 sec |
0.0010 in/in @Time 24.0 hour |
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0036 cm/cm @Time 86400 sec |
0.0036 in/in @Time 24.0 hour |
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 185 MPa | 26800 psi | Type I, 5 mm/min; ASTM D638 |
| Elongation at Break | 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 |
| Tensile Modulus | 21.0 GPa | 3050 ksi | 5 mm/min; ASTM D638 |
| Flexural Strength | 260 MPa | 37700 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 18.0 GPa | 2610 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 0.700 J/cm | 1.31 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.00 J/cm | 9.37 ft-lb/in | ASTM D4812 |
| Dart Drop, Total Energy | 10.0 J @Temperature 23.0 °C |
7.38 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
7.78 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| CTE, linear, Transverse to Flow | 35.0 µm/m-°C @Temperature -30.0 - 30.0 °C |
19.4 µin/in-°F @Temperature -22.0 - 86.0 °F |
ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C @Thickness 3.20 mm |
187 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
UL 94 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycoloy® C8080REC PC+ABS
- SABIC Innovative Plastics LNP Lubricomp RCP36XXQ PA 66 (Europe-Africa-Middle East)
- Solvay Specialty Polymers Tecnoflon® N 535 Fluoroelastomer
- Techmer ES HiFill® PA6/6 GB25 L BK 25% Glass Bead Filler
- Teknor Apex Telcar® OBC 4864A Thermoplastic Elastomer
- Ter Hell Plastic Terez® PA/PP 7500 GF 7/1 Polyamide/Polypropylene
- Diapolyacrylate Shinko-Lac® U400B Transparent ABS
- 3M Scotchcal™ 3632-25 Translucent Film
- ArcelorMittal Zagnelis™ ZM90 Double-sided ZnMgAl galvanized steel
Copyright © lookpolymers.com All Rights Reserved