Gromax BFG15-DN00N1 Nylon 6 16% Glass Filled (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax BFG15-DN00N1 Nylon 6 16% Glass Filled (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ISO 1183 |
| Moisture Absorption | 1.10 % | 1.10 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm @Temperature 80.0 °C |
0.0070 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Temperature 80.0 °C |
0.010 in/in @Temperature 176 °F |
60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 108 MPa | 15600 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 4.6 % | 4.6 % | 50 mm/min; ISO 527 |
| Tensile Modulus | 6.10 GPa | 885 ksi | 1 mm/min; ISO 527-1,-2 |
| Flexural Strength | 190 MPa | 27600 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 6.28 GPa | 910 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 4.10 kJ/m² | 1.95 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | 3.50 J/cm² @Temperature 23.0 °C |
16.7 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 0.460 J/cm² @Temperature 23.0 °C |
2.19 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 213 °C | 415 °F | ISO 75-1,-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 203 °C | 397 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- Performance Polymers IPS II PPL-C4150 PEKK (Polyetherketoneketone) Linear 30 % Glass Fiber Reinforced Molding Grade
- Lotte Chemical Titan TITANPRO® PD943 Polypropylene homopolymer
- Guarniflon TENFIL TF 200 Polytetrafluoroethylene Thread Sealant
- Techmer ES HiFill® HDPE GF30 A1 30% Glass Filled
- Saint-Gobain CHR® M887 Polyester Film Backing Silicone Adhesive Pressure Sensitive Tape
- Saint-Gobain CHR® SGB6-06(R) CHEMLAM Brown Glass-PTFE Backing Silicone Adhesive Pressure Sensitive Tape
- Styron Magnumâ„¢ 758HP ABS, High Heat, High Impact
- Colorite Polymers 1194B General Purpose Vinyl Compound
- Aaron Industries AAROLENE® ARPP C 200-3 Polypropylene Compounded Resin
Copyright © lookpolymers.com All Rights Reserved