Gromax ATE70-FN00N1 Nylon 6 (Dry)
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Gromax |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gromax ATE70-FN00N1 Nylon 6 (Dry).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Gromax Enterprises Corp.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.06 g/cc | 1.06 g/cc | ISO 1183 |
| Moisture Absorption | 1.40 % | 1.40 % | ISO 62 |
| Maximum Moisture Content | 0.10 | 0.10 | Karl Fischer |
| Linear Mold Shrinkage, Flow | 0.019 cm/cm | 0.019 in/in | 60x60x2 mm; ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.020 cm/cm | 0.020 in/in | 60x60x2 mm; ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 69 | 69 | [N/mm<sup>2<sup>]; ISO 7619 |
| Tensile Strength | 44.1 MPa | 6400 psi | 50 mm/min; ISO 527-1,-2 |
| Elongation at Break | 90 % | 90 % | 50 mm/min; ISO 527 |
| Flexural Strength | 65.0 MPa | 9430 psi | 5 mm/min; ISO 178 |
| Flexural Modulus | 1.62 GPa | 235 ksi | 5 mm/min; ISO 178 |
| Izod Impact, Notched | >= NB | >= NB | 5 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 80.0 kJ/m² | 38.1 ft-lb/in² | ISO 180-1A |
| Charpy Impact Unnotched | NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179-1eU |
| Charpy Impact, Notched | 2.10 J/cm² @Temperature -30.0 °C |
9.99 ft-lb/in² @Temperature -22.0 °F |
ISO 179-1A |
| 8.50 J/cm² @Temperature 23.0 °C |
40.4 ft-lb/in² @Temperature 73.4 °F |
ISO 179-1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 260 °C | 500 °F | 10°C/min; ISO 11357-1,-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | ISO 75-1,-2 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 270 - 280 °C | 518 - 536 °F | ISO 294 |
| Mold Temperature | 80.0 - 120 °C | 176 - 248 °F | ISO 294 |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 2.00 - 6.00 hour | 2.00 - 6.00 hour |
Users viewing this material also viewed the following:
- PolyOne Versaflex™ CL2050 Thermoplastic Elastomer (TPE)
- Pyrotek A-5C Fiberglass Fabric
- Premix Thermoplastics PRE-ELEC® PE 1270 (discontinued **)
- PolyOne Edgetek® AT-000/000 HI5 Natural NA Acetal (POM) Copolymer
- Saint-Gobain CHR® A603 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Teknor Apex APEX® 90-A472R-95-NT Polyvinyl Chloride, Flexible
- Techmer ES Plastiblend® ABS/PBT GF20
- ExxonMobil Label-Lyte® 85 LP-200M Mirror Finish, Metallized, White Opaque OPP for Water-based Patch Label Applications
- SABIC Innovative Plastics LNP THERMOCOMP PFB91S PA 6
Copyright © lookpolymers.com All Rights Reserved