- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Gichem GILAC H120X6/VOU ABS Flame Retardant (discontinued **)
Gichem GILAC H120X6/VOU ABS Flame Retardant (discontinued **)
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Gichem GILAC H120X6/VOU ABS Flame Retardant
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
ABS self-extinguishing class V0 with better fluidity and UV resistance. Medium injection speed.Information provided by GICHEM Gruppo Industriale Chimico
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min | 30 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 42.0 MPa | 6090 psi | ASTM D638 |
| Elongation at Yield | 7.0 % | 7.0 % | ASTM D638 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ASTM D648 |
| Vicat Softening Point | 90.0 °C | 194 °F | ASTM D1525/A |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
|
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Flammability Test | 75 | 75 | [°C] Bilia; IEC 331 |
| Oxygen Index | 27 % | 27 % | ASTM D2863 |
| Glow Wire Test | 960 °C | 1760 °F | IEC 695-2-1 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Middle Barrel Temperature | 220 - 230 °C | 428 - 446 °F | |
| Mold Temperature | 50.0 - 70.0 °C | 122 - 158 °F | |
| Drying Temperature | 80.0 °C | 176 °F | 2 hours |
Users viewing this material also viewed the following:
- Parker Chomerics CHO-SHIELD® 611 Part B Coating Catalyst
- PTS Trilac® FR3800 Flame Retardant ABS Resin, RoHS Compliant
- Ineos ABS NOVODUR® P2L-AT ABS, Injection Grade (discontinued **)
- Indium Corp. Indalloy 143 Lead Solder Alloy
- Henkel Hysol EA 9309.3NA Paste Adhesive System
- SABIC Innovative Plastics ULTEM 9075 PEI (Europe-Africa-Middle East)
- CeramTec SL 303 Silicon Nitride, SiAION+SiC
- Dymax EMAX 10002 Voil Coil Assembly Disk Drive Adhesive
Copyright © lookpolymers.com All Rights Reserved