GEHR Plastics PPS Polyphenylene Sulfide

Category	Polymer , Thermoplastic , Polyphenylene Sulfide (PPS)
Manufacturer	GEHR Plastics Inc
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	GEHR Plastics PPS Polyphenylene Sulfide.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The linear polyphenylensulfide belongs to the semi-crystalline materials and offers a very high mechanical capacity, thermal and chemical resistance distinguished at the same time, high dimensional stability, and creep strength. The LOI belongs to the highest of polymers. By the reinforcement with glass polymers strength is achieved, which is comparable with light metal. PPS closes the gap between the technical synthetics and PEEK with its strength and economy.Propertiesvery high strength and rigidityhigh hardnesshigh thermostabilityhigh dimensional stabilityvery high chemical resistancevery good insulating propertieshigh weather resistancehigh resistance to hydrolysisApplications include components in machine-making, pump parts, fan parts, impellers, parts in the fuel and automotive sector.

Physical Properties	Metric	English	Comments
Specific Gravity	1.35 g/cc	1.35 g/cc	ISO 1183
Water Absorption	0.020 %	0.020 %	ISO 62

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell M	95	95
Tensile Strength at Break	72.0 MPa	10400 psi	ISO 527
Tensile Strength, Yield	88.0 MPa	12800 psi	ISO 527
Elongation at Break	21 %	21 %	ISO 527
Elongation at Yield	3.4 %	3.4 %	ISO 527
Modulus of Elasticity	4.15 GPa	602 ksi	ISO 527
Flexural Strength	141 MPa	20500 psi	3.5%; ISO 178
Charpy Impact Unnotched	>= 25.0 J/cm²	>= 119 ft-lb/in²	ISO 179
Coefficient of Friction	0.40	0.40	DIN 53375

Thermal Properties	Metric	English	Comments
CTE, linear	53.0 µm/m-°C @Temperature 20.0 °C	29.4 µin/in-°F @Temperature 68.0 °F	DIN 53752
Thermal Conductivity	0.250 W/m-K	1.74 BTU-in/hr-ft²-°F	DIN 52612
Maximum Service Temperature, Air	150 °C	302 °F
Deflection Temperature at 1.8 MPa (264 psi)	115 °C	239 °F	ISO 75
Flammability, UL94	V-0	V-0

Electrical Properties	Metric	English	Comments
Volume Resistivity	>= 1.00e+11 ohm-cm	>= 1.00e+11 ohm-cm	VDE 0303
Surface Resistivity per Square	>= 1.00e+15 ohm	>= 1.00e+15 ohm	VDE 0303
Dielectric Constant	3.2 @Frequency 1.00e+6 Hz	3.2 @Frequency 1.00e+6 Hz	DIN 53483
Dielectric Strength	18.0 kV/mm	457 kV/in	VDE 0303
Comparative Tracking Index	125 V	125 V	CTI; IEC 60112

Descriptive Properties	Value	Comments
Acid Resistance	yes
Aromatic Resistance	limited
Bondability	yes
CKW Resistance	yes
Color	Natural
Hydrocarbonate Resistance	yes
Hydroxide Resistance	limited
Ketone Resistance	yes
Physiological indifference according	yes
Resistance Against Hot Water	yes
UV Stabilization	yes