Vicone High Performance Rubber VicoFluor™ 06FK-BR High Performance Fluoroelastomer Rubber
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Vicone High Performance Rubber |
| Trade Name | VicoFluor™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Vicone High Performance Rubber VicoFluor™ 06FK-BR High Performance Fluoroelastomer Rubber.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Meets ASTM D2000 fluoroelastomer 60 Durometer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.11 g/cc | 0.0762 lb/in³ | ASTM D297 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 59 | 59 | ASTM D2240 |
| Tensile Strength | 12.2 MPa | 1770 psi | ASTM D412 |
| Elongation at Break | 303 % | 303 % | ASTM D412 |
| Compressive Modulus | 0.00550 GPa @Strain 5 % |
0.798 ksi @Strain 5 % |
ISO-7743 |
| 0.00640 GPa @Strain 10 % |
0.928 ksi @Strain 10 % |
ISO-7743 | |
| 0.00730 GPa @Strain 20 % |
1.06 ksi @Strain 20 % |
ISO-7743 | |
| 0.00780 GPa @Strain 25 % |
1.13 ksi @Strain 25 % |
ISO-7743 | |
| Compression Set | 22 % @Temperature 200 °C, Time 79200 sec |
22 % @Temperature 392 °F, Time 22.0 hour |
ASTM D395 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Brown | |
| Effect of Liquids - Change in Elongation (%) | -22 | ASTM D471 |
| Effect of Liquids - Change in Hardness (%) | -3 | ASTM D471 |
| Effect of Liquids - Change in Tensile Strength (%) | -26 | ASTM D471; 23°C; 70 h |
| Effect of Liquids - Change in Volume after Oil Immersion (%) | 4.5 | ASTM D471 |
| Heat Aging - Change in Elongation (%) | -8 | ASTM D573; 275°C; 70h |
| Heat Aging - Change in Hardness (%) | 5 | ASTM D573; 275°C; 70h |
| Heat Aging - Change in Tensile Strength (%) | -11 | ASTM D573; 275°C; 70h |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 6-8438-1 Polyamide 12, with glass fiber
- Momentive Performance Materials Siloprenâ„¢ LSR 2735/30 Liquid Silicone Rubber - Self-Bonding / Self-Lubricating
- HP Alloys Alloy B-2, Solution Treated, 30% Cold Worked
- Solvay TECHNYL® A 21T2 V25 PA66, 25% glass fiber, Conditioned
- SABIC Innovative Plastics ULTEM HU2310 PEI (Europe-Africa-Middle East)
- Westlake ELEVATE™ EF529 18.5% Ethylene Vinyl Acetate Copolymer
- Unitika A1025GO PA6, Flame Retardant, Dry
- Chengdu Polyster H8570 Thermoplastic Polyether-ester Elastomer (TPEE)
- Asahi Kasei Thermylene® P6-10FG-Y950 10% Glass Fiber Reinforced, Lubricated
Copyright © lookpolymers.com All Rights Reserved