GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Dry

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled
Manufacturer GEHR Plastics Inc
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF GEHR Plastics PA 6.6-30GF Nylon 6.6, 30% Glass Fiber, Dry.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Polyamide shows both a high thermostability and high stiffness, hardness and toughness. These are some of the main characteristics. Due to the fact, that the good mechanical characteristics will be achieved only after conditioning, this material must be conditioned again after annealing. In addition, this conditioning occurs with a longer storage in air automatically. This polyamide has the highest hardness, rigidity, and a good resistance to wear and heat deflection temperature.Properties:high impact strength and stiffnesshigh impact and notching impact strengthhigh heat deflection temperaturegood at dampeninggood glide and limp home charactersgood chemical stability against organic solvents and fuelssize alteration by humidity absorption must be considereddimension stability, electrical and mechanical properties may become affected by absorbing moisture or waterApplications include bearing parts, gear wheels, pump parts, sliding rails, castors, and fittings.
Physical Properties Metric English Comments
Specific Gravity 1.29 g/cc
1.29 g/cc
ISO 1183
Water Absorption 1.7 %
1.7 %
ISO 62
Mechanical Properties Metric English Comments
Ball Indentation Hardness 165 MPa
23900 psi
ISO 2039
Tensile Strength at Break 100 MPa
14500 psi
ISO 527
Elongation at Break 5.0 %
5.0 %
ISO 527
Modulus of Elasticity 5.90 GPa
856 ksi
ISO 527
Charpy Impact Unnotched >= 5.00 J/cm²
>= 23.8 ft-lb/in²
ISO 179
Charpy Impact, Notched 0.600 J/cm²
2.86 ft-lb/in²
ISO 179
Thermal Properties Metric English Comments
CTE, linear 60.0 µm/m-°C

@Temperature 20.0 °C
33.3 µin/in-°F

@Temperature 68.0 °F
DIN 53752
Thermal Conductivity 0.300 W/m-K
2.08 BTU-in/hr-ft²-°F
DIN 52612
Maximum Service Temperature, Air 110 °C
230 °F
Deflection Temperature at 1.8 MPa (264 psi) 150 °C
302 °F
ISO 75
Minimum Service Temperature, Air -20.0 °C
-4.00 °F
Flammability, UL94 HB
HB
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+14 ohm-cm
>= 1.00e+14 ohm-cm
VDE 0303
Surface Resistivity per Square >= 1.00e+13 ohm
>= 1.00e+13 ohm
VDE 0303
Dielectric Constant 3.6

@Frequency 1.00e+6 Hz
3.6

@Frequency 1.00e+6 Hz
DIN 53483
Dielectric Strength 30.0 kV/mm
762 kV/in
VDE 0303
Dielectric Loss Index 0.014

@Frequency 1.00e+6 Hz
0.014

@Frequency 1.00e+6 Hz
DIN 53483
Comparative Tracking Index 475 V
475 V
CTI; IEC 60112
Descriptive Properties Value Comments
Acid Resistance yes
Aromatic Resistance yes
Bondability yes
CKW Resistance no
Color Black
Hydrocarbonate Resistance yes
Hydroxide Resistance yes
Ketone Resistance yes
Physiological indifference according no
Resistance Against Hot Water yes
UV Stabilization yes