Lehmann & Voss LUVOCOM® 1/XCF/25 Polyamide 66, with carbon fiber, heat stabilized
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Carbon Fiber Filled |
| Manufacturer | Lehmann & Voss & Co. |
| Trade Name | LUVOCOM® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Lehmann & Voss LUVOCOM® 1/XCF/25 Polyamide 66, with carbon fiber, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Applications: Automotive industry, textile- and office machinery, apparatus- and precision engineering.High-strength and high-stiff parts; low coefficient of expansion.Reduced moment of inertia compared with metal parts.Electrically conductive, suitable for continuous discharging of statically generated electricity.High dimensionally stable precision parts with low warpage and narrow tolerance range.Gear parts for automotive appliances, control disks, cams, sliding elements.Information provided by Lehmann & Voss & Co.KG
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.25 g/cc | 1.25 g/cc | ISO 1183 |
| Water Absorption | <= 1.0 % | <= 1.0 % | 23°C/24h |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Stress | 295 MPa | 42800 psi | |
| Elongation at Yield | 2.5 % | 2.5 % | |
| 3.1 % | 3.1 % | flexural | |
| Modulus of Elasticity | 21.0 GPa | 3050 ksi | |
| Flexural Strength | 420 MPa | 60900 psi | |
| Flexural Modulus | 18.0 GPa | 2610 ksi | |
| Charpy Impact Unnotched | 9.00 J/cm² | 42.8 ft-lb/in² | edgewise; ISO 179 1eU |
| Charpy Impact, Notched | 1.10 J/cm² | 5.23 ft-lb/in² | ISO 179 1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 14.0 µm/m-°C | 7.78 µin/in-°F | DIN 53752 |
| Thermal Conductivity | 0.500 W/m-K | 3.47 BTU-in/hr-ft²-°F | DIN 52612 |
| Maximum Service Temperature, Air | 120 °C | 248 °F | |
| 160 °C | 320 °F | short term | |
| Deflection Temperature at 1.8 MPa (264 psi) | 250 °C | 482 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | <= 10000 ohm | <= 10000 ohm | |
| Insulation Resistance | <= 10000 ohm | <= 10000 ohm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 290 °C | 554 °F | mass temp |
| Nozzle Temperature | 280 - 300 °C | 536 - 572 °F | |
| Zone 1 | 290 - 310 °C | 554 - 590 °F | |
| Zone 2 | 290 - 310 °C | 554 - 590 °F | |
| Zone 3 | 290 - 310 °C | 554 - 590 °F | |
| Mold Temperature | 90.0 - 120 °C | 194 - 248 °F | |
| Drying Temperature | 75.0 °C @Time 21600 - 57600 sec |
167 °F @Time 6.00 - 16.0 hour |
Dehumidifying dryer |
| 105 °C @Time 14400 - 21600 sec |
221 °F @Time 4.00 - 6.00 hour |
Vacuum Dryer |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | natural color (black) |
Users viewing this material also viewed the following:
- Lehmann & Voss LUVOCOM® 1105-8534 PEEK, with mineral filler
- Lord Adhesives 363 Two-Component, Fast Set, Modified Epoxy Adhesive
- Gwent Electronic Materials C2000215D4 Silver / Silver Chloride Paste
- Borealis Daploy™ WB130HMS High Melt Strength Polypropylene for Foam Extrusion
- Polyram PlusTek PA4501G6 Nylon 66, 30% Glass Fiber Reinforced, Low Friction
- ChevronTexaco Elite-Cut® NH Metal Working Fluid
- ExxonMobil LDPE LD 151GZ Low Density Polyethylene Resin
- 3M 1126 EMI Shielding Tape
- 3M Dyneon™ FC 2122 Fluoroelastomer
- Arlon 51986R020 0.020" (0.508 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved