Firestone CL200-001 Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Firestone |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Firestone CL200-001 Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Natural color. Not heat stabilized or modified. Lubricated. Chip size is 2 x 3.5 mm.Information provided by Firestone
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Viscosity Measurement | 3.2 | 3.2 | Relative Viscosity; Sulfuric Acid |
| 82 | 82 | Relative Viscosity; Formic Acid | |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 83.0 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 60 % | 60 % | ASTM D638 |
| Flexural Yield Strength | 103 MPa | 14900 psi | ASTM D790 |
| Flexural Modulus | 2.76 GPa | 400 ksi | ASTM D790 |
| Izod Impact, Notched | 0.540 J/cm | 1.01 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 220 °C | 428 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Middle Barrel Temperature | 238 - 249 °C | 460 - 480 °F | |
| Front Barrel Temperature | 243 - 260 °C | 470 - 500 °F | |
| Nozzle Temperature | 249 - 260 °C | 480 - 500 °F | |
| Melt Temperature | 249 - 260 °C | 480 - 500 °F | |
| Mold Temperature | 48.9 - 82.2 °C | 120 - 180 °F | |
| Drying Temperature | 73.9 °C | 165 °F | |
| Dry Time | 4 hour | 4 hour | |
| Moisture Content | <= 0.080 % | <= 0.080 % |
Users viewing this material also viewed the following:
- Materion BrushCAST® 3C High Conductivity Casting Alloy (As Cast)
- Sylvin Technologies 8940-85 Natural PVC Extrusion Compound
- Techmer ES Elastoblend® PA6/6 GF43 IM HS L BK
- Styron XU 36535.00 Formulated SB
- A. Schulman POLYTROPE™ TPP 524E Extrusion Grade Olefinic Thermoplastic Elastomer
- A. Schulman POLYPUR™ FPU 1550 Thermoplastic Polyurethane Compound
- ChevronTexaco Cygnus® 220 Gear Oil
- Colorite Polymers 7511G-015 (Extrustion), 7512G-015 (Molding) Radiation Sterilizable Vinyl Compound
- SABIC Innovative Plastics LNP THERMOTUF PF006I PA 6
Copyright © lookpolymers.com All Rights Reserved