Fiberfil® PP-60/TC/40/OP WT2595 Polypropylene Homopolymer, 40% Talc Filled, high opacity
| Category | Polymer , Thermoplastic , Polypropylene (PP) |
| Manufacturer | FiberFil |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Fiberfil® PP-60/TC/40/OP WT2595 Polypropylene Homopolymer, 40% Talc Filled, high opacity.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by FIBERFIL Engineered Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.30 g/cc | 1.30 g/cc | ASTM D792 |
| Water Absorption | 0.030 % | 0.030 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.0050 - 0.0060 cm/cm @Thickness 3.17 mm |
0.0050 - 0.0060 in/in @Thickness 0.125 in |
ASTM D955 |
| 0.0060 - 0.0070 cm/cm @Thickness 6.35 mm |
0.0060 - 0.0070 in/in @Thickness 0.250 in |
ASTM D955 | |
| Melt Flow | 6.0 g/10 min | 6.0 g/10 min | 230/2.16 (typical); ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 90 - 100 | 90 - 100 | ASTM D785 |
| Tensile Strength, Yield | 29.6 MPa | 4300 psi | ASTM D638 |
| Elongation at Yield | 15 % | 15 % | ASTM D638 |
| Tensile Modulus | 5.17 GPa | 750 ksi | ASTM D638 |
| Flexural Strength | 60.7 MPa | 8800 psi | ASTM D790 |
| Flexural Modulus | 4.21 GPa | 610 ksi | Tangent; ASTM D790 |
| Izod Impact, Notched | 0.267 J/cm @Thickness 3.17 mm |
0.500 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 143 °C | 290 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 104 °C | 220 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 199 - 210 °C | 390 - 410 °F | |
| Middle Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Front Barrel Temperature | 182 - 199 °C | 360 - 390 °F | |
| Nozzle Temperature | 182 - 193 °C | 360 - 380 °F | |
| Melt Temperature | 199 - 232 °C | 390 - 450 °F | |
| Mold Temperature | 32.2 - 71.1 °C | 90.0 - 160 °F | |
| Drying Temperature | 76.7 °C | 170 °F | Drying not normally required |
| Dry Time | 2 hour | 2 hour | Drying not normally required |
| Moisture Content | <= 0.20 % | <= 0.20 % | recommended for molding |
| Back Pressure | 0.000 - 0.689 MPa | 0.000 - 100 psi |
Users viewing this material also viewed the following:
- Nilit FRIANYL A63 KV15 Nylon 6.6 for injection molding, 15% glass ball reinforced
- PTS Tristar® PC-30GF 30% Glass Reinforced Polycarbonate With Release
- Hyosung Topilene R701G PP
- Solvay Chemicals SOLKANE® 22M
- Saint-Gobain CHR® A662 Aluminum Foil Backing Acrylic Adhesive Pressure Sensitive Tape
- Silikony Polskie Oilsil Silicone Release Agent
- EMS-Grivory Grivory® BK-50 PA6-GB50
- EPICHEM Epilac R ABS 17% GF ABS, 17% Glass Fiber
- Abatron AboCast 8708-10 One-Component Structural/Dielectric Epoxy
Copyright © lookpolymers.com All Rights Reserved