A. Schulman ComAlloy Lubrilon® 635 Nylon 6/6, Carbon Fiber/PTFE Filled, Proprietary Lubricant Package

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Carbon Fiber/PTFE Filled
Manufacturer A. Schulman ComAlloy
Trade Name Lubrilon®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF A. Schulman ComAlloy Lubrilon® 635 Nylon 6/6, Carbon Fiber/PTFE Filled, Proprietary Lubricant Package.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by the manufacturer, ComAlloy International Company. High performance and excellent lubricity with minimal surface wear.The ComAlloy product line has been integrated into the A Schulman product line.
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
Linear Mold Shrinkage 0.0010 cm/cm
0.0010 in/in
ASTM D955
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115
115
ASTM D785
Tensile Strength, Ultimate 181 MPa
26300 psi
ASTM D638
Elongation at Break 4.0 %
4.0 %
ASTM D638
Flexural Strength 281 MPa
40800 psi
ASTM D790
Flexural Modulus 18.3 GPa
2650 ksi
ASTM D790
Izod Impact, Notched 0.530 J/cm
0.993 ft-lb/in
ASTM D256
Izod Impact, Unnotched 5.23 J/cm
9.80 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
Melting Point 255 - 275 °C
491 - 527 °F
Deflection Temperature at 0.46 MPa (66 psi) 262 °C
504 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 251 °C
484 °F
ASTM D648
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
Approximate middle barrel temperature.