FKuR Kunststoff Bio-Flex® S 5630 Compostable PLA Blend

Category Polymer , Renewable/Recycled Polymer , Thermoplastic , Polylactic Acid (PLA) Biopolymer
Manufacturer FKuR Kunststoff GmbH
Trade Name Bio-Flex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF FKuR Kunststoff Bio-Flex® S 5630 Compostable PLA Blend.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
The BIO-FLEX® trade name indicates blends of co-polyester and PLA* with, depending on the particular grade, a very high content of natural resource material. BIO-FLEX® does not contain any starch or starch derivatives. Bioplastics generally replace conventional materials such as low density polyethylene (LDPE), high density polythene (HDPE) as well as polystyrene (PS) and polypropylene (PP). For packaging applications these materials need to be converted into film which is as thin as possible while maintaining high tensile strength. Depending on the specific application, packaging films have to provide a high barrier against humidity, oxygen and aromas or alternatively provide adequate permeability (“breathability”).Information Provided by FKuR Kunststoff GmbH
Physical Properties Metric English Comments
Bulk Density 0.895 g/cc
0.0323 lb/in³
ISO 60
Density 1.55 g/cc
0.0560 lb/in³
ISO 1183
Melt Flow 8.0 - 10 g/10 min

@Load 2.16 kg,
Temperature 190 °C
8.0 - 10 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 29.0 MPa
4210 psi
ISO 527
Tensile Strength 32.0 MPa
4640 psi
ISO 527
Elongation at Break 9.0 %
9.0 %
ISO 527
Elongation at Yield 6.0 %
6.0 %
ISO 527
Tensile Modulus 2.16 GPa
313 ksi
ISO 527
Flexural Strength 46.0 MPa
6670 psi
at 3.5% strain; ISO 178
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Charpy Impact Unnotched 5.10 J/cm²

@Temperature 23.0 °C
24.3 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eU
Charpy Impact, Notched 0.300 J/cm²

@Temperature 23.0 °C
1.43 ft-lb/in²

@Temperature 73.4 °F
ISO 179-1/1eA
Thermal Properties Metric English Comments
Melting Point 140 - 160 °C
284 - 320 °F
ISO 3146-C
Deflection Temperature at 0.46 MPa (66 psi) 68.0 °C
154 °F
ISO 75 B
Vicat Softening Point 105 °C
221 °F
A; ISO 306
Descriptive Properties Value Comments
Melt Volume Flow (cm3/10 min) 8-10
ISO 1133; 190°C, 2.16kg