Material Notes:
Ceramite is a family of wear resistant castables with a unique combination of high wear resistance, thermal resistance and mechanical strength. Ceramite is produced and supplied to end users world wide, both as mortars and as various precast components. Ceramite can easily be mixed, cast and shaped in any size and is thus comfortably to work with in-situ. Ceramite can be used in within a wide range of temperatures and applications exposed to thermal shock conditions in industries like for example aluminum, cement and ferro.Applications: Floor Tile, Hearth/Furnace Tile, Furnace Sills & Doors, Lintels, Pipe and Duct Linings, Feed Tubes, Troughs/Launders, Ladles, Dampers, Nozzle Blasters, Crucible Linings, Vortex, Burner Tip Cooler Plates, Nose Ring, Electrical Insulation, Cold Wear AreasSpecific Notes on This Grade: The basic all-round castable with good thermal and electrical insulating properties. A castable widely used in aluminum, ferro alloys, mining, cement, and steel industries. Good references as floor times, crucible linings, impact plates, lining of furnace gates etc.Information provided by Stellar Canada.
Physical Properties Metric English Comments
Bulk Density 2.87 g/cc
0.104 lb/in³
As Placed
Porosity 13.2 %
13.2 %
Apparent
Mechanical Properties Metric English Comments
Modulus of Rupture 0.01500 GPa
2.176 ksi
Hot, prefired at 1832°F/24 hours (1000°C)
Flexural Strength 11.82 MPa

@Temperature 1200 °C
1714 psi

@Temperature 2192 °F
after Firing; ASTM-349
17.1 MPa

@Temperature 850.0 °C
2480 psi

@Temperature 1562 °F
after Firing; ASTM-349
19.30 MPa

@Temperature 1000 °C
2799 psi

@Temperature 1832 °F
after Firing; ASTM-349
23.1 MPa

@Temperature 500 °C
3350 psi

@Temperature 932 °F
after Firing; ASTM-349
Compressive Strength 166.01 MPa
24077 psi
Cold Crushing after 1560°F
103.00 MPa

@Temperature 1200 °C
14939 psi

@Temperature 2190 °F
after Firing; ASTM C-349
133.0 MPa

@Temperature 850 °C
19290 psi

@Temperature 1560 °F
after Firing; ASTM C-349
145.00 MPa

@Temperature 1000 °C
21031 psi

@Temperature 1830 °F
after Firing; ASTM C-349
197.00 MPa

@Temperature 500 °C
28573 psi

@Temperature 932 °F
after Firing; ASTM C-349
207.00 MPa

@Temperature 20.0 °C
30023 psi

@Temperature 68.0 °F
after 7 days
Thermal Properties Metric English Comments
Thermal Conductivity 1.70 W/m-K

@Temperature 300 °C
11.8 BTU-in/hr-ft²-°F

@Temperature 572 °F
1.77 W/m-K

@Temperature 600.0 °C
12.3 BTU-in/hr-ft²-°F

@Temperature 1112 °F
2.16 W/m-K

@Temperature 900.0 °C
15.0 BTU-in/hr-ft²-°F

@Temperature 1652 °F
Maximum Service Temperature, Air 1200 °C
2200 °F
Component Elements Properties Metric English Comments
Al2O3 79 %
79 %
CaO 6.3 %
6.3 %
Fe2O3 1.08 %
1.08 %
K2O 0.16 %
0.16 %
MgO 0.090 %
0.090 %
Na2O 0.070 %
0.070 %
SiO2 11 %
11 %
TiO2 3.0 %
3.0 %
Descriptive Properties Value Comments
Application Prefired
Precast Shapes