Eurotec® Tecomid® NT40 NL MB PPA, impact modified, heat stabilized, natural
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), High Impact |
| Manufacturer | Eurotec |
| Trade Name | Tecomid® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Eurotec® Tecomid® NT40 NL MB PPA, impact modified, heat stabilized, natural.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Eurotec®
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Moisture Absorption | 2.20 % @Temperature 23.0 °C |
2.20 % @Temperature 73.4 °F |
50% RH; ISO 960 |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm | 0.017 in/in | Eurotec |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | Eurotec |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ISO 527 |
| Elongation at Break | 10 % | 10 % | ISO 527 |
| Tensile Modulus | 2.75 GPa | 399 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 18.0 kJ/m² @Temperature -30.0 °C |
8.57 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 20.0 kJ/m² @Temperature 23.0 °C |
9.52 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 315 °C | 599 °F | [10 K/min], ISO 11357 |
| Deflection Temperature at 1.8 MPa (264 psi) | 115 °C | 239 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 0.750 mm |
HB @Thickness 0.0295 in |
|
| HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | Solution A; IEC 60112 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 320 - 340 °C | 608 - 644 °F | |
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat |
| Mold Temperature | 70.0 - 90.0 °C | 158 - 194 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 |
| Hold Pressure | 40.0 - 80.0 MPa | 5800 - 11600 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Back Pressure | Low | |
| Injection Speed | Medium - Fast |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® DMX2415 PC (Asia Pacific)
- Honeywell Aegis™ PL220HS High Viscosity, Heat Stabilized, Flexible Nylon 6 (discontinued **)
- Hong Kun Group AO B225 Antioxidant
- IRPC Polimaxx Polene 2300K Polypropylene Block Copolymer
- Techmer ES HiFill® ABS GB15 15% Glass Bead Filler
- Covestro Apec® HT KU 1-9357/2 High-Heat Polycarbonate, 20% Glass Fiber
- Diamond Polymers PC 1035L Impact Modified, Polycarbonate, Injection Molding Grade
- DuPont Teijin Films Melinex® 542 Polyester Film
- BASF Ultramid® B3ZG6 BK 30564 30% Glass Filled PA6-1 (Conditioned)
Copyright © lookpolymers.com All Rights Reserved